Usage
It’s suitable for transportation of hard and sharp materials in
larger drop height occasions, in lines of mines, ports,
electricity, metallurgy, chemical industry, coalmines, etc.
Characteristics
1.The anti- tear conveyor belt has highly extensible transverse
steel cords or polyester cords evenly arranged in the top cover (or
both top and bottom cover) of the steel cord carcass.
2.The anti-tear layer is perpendicular to the running direction of
belt.
3.When the belt conveys hard and sharp materials, the anti-tear
layer can stop it from being pierced. Even if the belt is pierced,
the anti-tear layer can still prevent it from being torn.
Standard Specifications
| Model | Tensile Strength(N/mm) | Cord Pitch (mm) | Cord Diameter (mm) | Min Cover thickness (mm) | Width (mm) |
| ST630 | 630 | 10 | 3 | 4 | 800-2400 |
| ST800 | 800 | 10 | 3.5 | 4 | |
| ST1000 | 1000 | 12 | 4 | 4 | |
| ST1250 | 1250 | 12 | 4.5 | 4 | |
| ST1600 | 1600 | 12 | 5 | 4 | |
| ST2000 | 2000 | 12 | 6 | 4 | |
| ST2500 | 2500 | 15 | 7.2 | 5 | |
| ST3150 | 3150 | 15 | 8.1 | 5.5 | |
| ST3500 | 3500 | 15 | 8.6 | 6 | |
| ST4000 | 4000 | 15 | 8.9 | 6.5 | |
| ST4500 | 4500 | 16 | 9.7 | 7 | |
| ST5000 | 5000 | 17 | 10.9 | 7.5 | |
| ST5400 | 5400 | 17 | 11.3 | 8 | |
| ST6300 | 6300 | 19.5 | 12.8 | 10 | |
| ST7000 | 7000 | 19.5 | 13.5 | 10 | |
| ST7500 | 7500 | 21 | 15 | 10 |
Note: Cover thickness, cord diameter, and cord pitch can be
manufactured according to customer’s requirements.
Cover Grades
| Grade | Tensile Strength(ISO37) Mpa
| Elongation at break min. (ISO37) % | Abrasion max. (ISO4649) mm³ |
| H | 24 | 450 | 120 |
| D | 18 | 400 | 100 |
| XTO D | 18 | 400 | 50 |
The values will help to determine the appropriate cover compound
for the application or for the materials carries. Reliable
assessment of the behavior of the covers in service for wear and
cut resistance cannot be determined from tensile strength, and
abrasion values alone.