Stellite 12 Hardfacing HVOF PTA Cobalt Based Alloy Powder For Sawteech Screw Fights
Product Description
WLCo-12 powder produces a deposit for high heat and corrosion resistance, with excellent wear properties. The Machineability, WLCo-12 powder makes it a good choice for knife cutting edges in the carpet, paper, and plastic industry. It could be considered as an intermediate alloy between WLCo-6 and WLCo-1. It contains a higher fraction of hard, brittle carbides than WLCo-6, and has increased resistance to lowangle erosion, abrasion, and severe sliding wear whilst retaining reasonable impact and cavitation resistance. It can be used at temperature up to 700˚C. WLCo-12 powder deposits provide resistance to all types of wear, including galling. It can be applied to all weldable steels, including stainless steels.
Common Names: Stellite 12 Polystel 12
Standard: AWS 5.21-2001 ERCoCr-B
CHEMICAL COMPOSITION(%)
| C | Si | Mn | Mo | Cr | W | Ni | Fe | Co |
| 1.4 | 1.30 | ≤1.00 | ≤1.00 | 30.00 | 8.5 | ≤3.00. | ≤3.00 | Rest |
CHARACTERISITIC
| Abrasion Resistance | Good |
| Impact Resistance | Good |
| Corrosion Resistance | Good |
| Hardness | HRC 44-50 |
| Deposit Layers | 2 MAX |
| Deposit Cross Checks | * No |
| Magnetic | No |
| Hot Wear Hardness | Good |
| Machineability | Carbide Tools |
Packing Details
Each bottle 5kg/bottles, 5 bottles pack in one carton,
then put cartons onto pallet or Box. OEM packing & label or customized packing methods available.
APPLICATIONS
High temperature and high-pressure valve
Used for pre-protection of plastics, paper-making, chemical fiber,
cutter and blade Outlet valve sealing surface
Scissor Blades, Knives, Twist Rolls
Saw Blades, Saw Blades and Tips, Saw Teeth, Chain saw bars
Guide Bars
Wood Cutting Tools
molten glass cutter
Type we could offer
| Trademark | Nominal Chemical Composition | HRC | Application | |||||||||
| C | Cr | Si | W | Ni | Fe | Mn | Mo | Co | B | |||
| WL Co1 | 2.45 | 30.0 | 1.0 | 13.0 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 50-58 | Valve seat insets, bearing, sawteeth, rotary ring, Pump Sleeves | |
| WL Co3 | 2.4 | 30.5 | 1.0 | 13.0 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 50-56 | Valve seat insets,steel mill guide roll, wearing panel of cracker blade, etc. | |
| WL Co4 | 1.0 | 31.0 | 1.0 | 14.0 | ≤3.0 | ≤1.0 | ≤0.5 | ≤0.5 | Bal. | 45-50 | Hot extrusion die, dry battery industry | |
| WL Co6 | 1.2 | 29.0 | 1.0 | 4.5 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 40-46 | Engine valve, high temperature valve, turbine blade | |
| WL Co12 | 1.4 | 30.0 | 1.3 | 8.5 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 44-50 | Pressure valves, sawteeth screw fights | |
| WL Co20 | 2.5 | 32.0 | 1.0 | 17.0 | ≤3.0 | ≤3.0 | ≤0.5 | ≤1.0 | Bal. | 54-59 | Wear plate, bearing sleeve, etc. | |
| WL Co21 | 0.2 | 27.0 | 1.0 | 0.2 | ≤3.0 | ≤2 | ≤1.0 | ≤5.5 | Bal. | 20-40 | Fluid valve seat, turbine blades, hot forging die | |
| WL Co25 | 0.05 | 20.0 | 1.0 | 15.0 | 10.0 | ≤2.0 | ≤1.5 | ≤1.0 | Bal. | 24 | High temperature and corrosion-resistant valve sealing surface, pressure casting dies, etc. | |
| WL Co31 | 0.5 | 26.0 | 1.0 | 7.5 | 10.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 30-35 | Extrusion die, steam turbine blade, etc. | |
| WL Co32 | 1.8 | 26.0 | 1.2 | 12.0 | 22.0 | ≤1.5 | ≤0.5 | ≤1.0 | Bal. | 40-45 | Engine inlet and exhaust valve | |
| WL Co190 | 3.2 | 26.0 | 1.0 | 14.0 | ≤1.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 54-60 | Petroleum drill bit, mining industry | |
| WL CoT400 | 0.08 | 8.5 | 2.6 | 1.5 | ≤1.5 | ≤1.0 | 28 | Bal. | 0.8 | 50-60 | Valve and roller path, plastic extruder in strongly corrosive | |
| WL CoT800 | 0.08 | 18.0 | 3.4 | ≤1.5 | 1.5 | ≤1.0 | 28 | Bal. | 0.8 | 52-58 | Valve and roller path, plastic extruder in strongly corrosive | |