Stellite 6 AWS A5.21 ERCoCr-A Hard Facing Rod Extrusion Screws Flights Tong Bits
Product Description
WLCo 6 cobalt based rod is the most widely used of the cobalt alloys. It is regarded as the industry standard for general-purpose wear resistance applications, has excellent resistance to many forms of mechanical and chemical degradation over a wide temperature range, and retains a reasonable level of hardness up to 500°C (930°F).
It also has good resistance to impact and cavitation erosion.
WL-Co6 is ideally suited to a variety of hardfacing processes and
can be turned with carbide tooling. Examples include valve seats
and gates, pump shafts and bearings, erosion shields, and rolling
couples. It is often used self-mated.
Another similar type is Co 6H rod, which has higher hardness.
Common Names: Stellite 6, BISHILITE (MHA) No.6, Weartech WT-6, Stoodite 6,
POLYSTEL 6, Hoganas 2537
Standard: AWS 5.21-2001, ERCoCr-A
Chemical Composition(%)
C | Si | Mn | Mo | Cr | W | Ni | Fe | Co |
1.15 | 1.00 | ≤1.00 | ≤1.00 | 29.00 | 4.5 | ≤3.00. | ≤3.00 | Rest |
Characterisitic
Abrasion Resistance | Good |
Impact Resistance | Good |
Corrosion Resistance | Good |
Hardness | HRC 40-46 |
Deposit Layers | 2 Max |
Deposit Cross Checks | * Possible |
Magnetic | No |
Hot Wear Hardness | Good |
Machineability | Carbide Tools |
Packing Details
For length 350mm 500mm pack in carton each 5kg
For 1000mm packing in 5kg tube, 4 tubes in one 20kg carton
For length more than 1000mm, pack in wooden box directly
Applications
Used to make motor spiracle, high temperature and high pressure
valve sealing surface Bearing Areas
Extrusion Screws Flights Tong Bits
Type We Could Offer
| Trademark | Nominal Chemical Composition | HRC | Application | |||||||||
| C | Cr | Si | W | Ni | Fe | Mn | Mo | Co | B | |||
| WL Co1 | 2.45 | 30.0 | 1.0 | 13.0 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 50-58 | Valve seat insets, bearing, sawteeth, rotary ring, Pump Sleeves | |
| WL Co3 | 2.4 | 30.5 | 1.0 | 13.0 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 50-56 | Valve seat insets,steel mill guide roll, wearing panel of cracker blade, etc. | |
| WL Co4 | 1.0 | 31.0 | 1.0 | 14.0 | ≤3.0 | ≤1.0 | ≤0.5 | ≤0.5 | Bal. | 45-50 | Hot extrusion die, dry battery industry | |
| WL Co6 | 1.2 | 29.0 | 1.0 | 4.5 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 40-46 | Engine valve, high temperature valve, turbine blade | |
| WL Co12 | 1.4 | 30.0 | 1.3 | 8.5 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 44-50 | Pressure valves, sawteeth screw fights | |
| WL Co20 | 2.5 | 32.0 | 1.0 | 17.0 | ≤3.0 | ≤3.0 | ≤0.5 | ≤1.0 | Bal. | 54-59 | Wear plate, bearing sleeve, etc. | |
| WL Co21 | 0.2 | 27.0 | 1.0 | 0.2 | ≤3.0 | ≤2 | ≤1.0 | ≤5.5 | Bal. | 20-40 | Fluid valve seat, turbine blades, hot forging die | |
| WL Co25 | 0.05 | 20.0 | 1.0 | 15.0 | 10.0 | ≤2.0 | ≤1.5 | ≤1.0 | Bal. | 24 | High temperature and corrosion-resistant valve sealing surface, pressure casting dies, etc. | |
| WL Co31 | 0.5 | 26.0 | 1.0 | 7.5 | 10.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 30-35 | Extrusion die, steam turbine blade, etc. | |
| WL Co32 | 1.8 | 26.0 | 1.2 | 12.0 | 22.0 | ≤1.5 | ≤0.5 | ≤1.0 | Bal. | 40-45 | Engine inlet and exhaust valve | |
| WL Co190 | 3.2 | 26.0 | 1.0 | 14.0 | ≤1.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 54-60 | Petroleum drill bit, mining industry | |
| WL CoT400 | 0.08 | 8.5 | 2.6 | 1.5 | ≤1.5 | ≤1.0 | 28 | Bal. | 0.8 | 50-60 | Valve and roller path, plastic extruder in strongly corrosive | |
| WL CoT800 | 0.08 | 18.0 | 3.4 | ≤1.5 | 1.5 | ≤1.0 | 28 | Bal. | 0.8 | 52-58 | Valve and roller path, plastic extruder in strongly corrosive | |