Due to our adoption of hot rolling process, the original casting
structure of the steel slab for making hot rolled pipe is
destroyed. This means that the crystalline grains of steel material
are refined, and the defects of the microstructure of steel slab
are eliminated, which results in improved mechanical performance
and denser microstructure of steel materials along the rolling
direction. |
Product Name | Stainless Steel Pipe/Tube | |||
Technology | Hot Rolled Industrial Stainless Steel Tube Cold Rolled Decorative Stainless Steel Pipe | |||
Material | 201, 202, 301, 302, 304, 304L, 310S, 316, 316L, 321, 430, 430A,
309S, 2205, 2507, 2520, 430 , 410, 440, 904Lect, Or Customized | |||
Thickness | 0.4-50 mm | |||
Length | 1-12 m | |||
Outer Diameter(OD) | 10-2000mm | |||
Standard | ASTM, JIS, GB, AISI, DIN, BS,EN | |||
Certifications | ISO 9001 BV SGS | |||
Packing | Industry standard packaging or according to client's requirement | |||
Brand | TISCO,ZPSS,Baosteel,POSCO,LISCO,YUSCO,Ansteel, QPSS,JISCO,HXSCO, Chengde,Yongjin,Tsingshan,Shouyang,HW | |||
Payment terms | 30%T/T in advance, the balance against the B/L copy | |||
Delivery time | Fast delievery in 7 days,up to order quantity | |||
Warehose Stcok | 5000 tons per month |
Chemical Composition
Specification | Grade | Chemical Composition(wt%) | ||||||
C | Mn | Ni | Cr | Mo | Ti | |||
ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 |
Properties
Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S (N/MM2) | T.S (N/MM2) | EL (%) | HRB | Specific Heat (J/g℃) | Modulus of Elasticity (KN/mm2) | ||
ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications
316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.
316Ti: Mainly used for industrial components.
|