304 Seamless AISI Standard 0.8mm Ss Square Pipe
Seamless steel tube, made of whole metal, without seams, so called
seamless steel tube.According to the production method, seamless
tube divided hot rolled tube, cold rolled tube, cold drawing tube,
extruded tube, top tube, etc .Our product is cold rolled or cold
drawing then honed or SRB(skived rolled burnished) ,the surface
polished some lathed. |
| Name | 304 Square Stainless Steel Tubing Seamless, stainless steel square tube | |||
| Items | ROUND SS SMLS PIPE | |||
| Standard | ASTM ,GB,DIN AISI | |||
| Material Grade | 201: Ni 0.7%--1% | |||
| 304: Ni 8%, Cr 18% | ||||
| 316L:Ni10%,Cr16% | ||||
| Outer Diameter | Round pipe9.5mm--813mm | |||
| Thickness | 0.8mm - 34mm | |||
| Length | 5.8m,6m, or as customers' request | |||
| Tolerance | a) Outer Diameter: +/- 0.2mm | |||
| b) Thickness: +/- 0.02mm | ||||
| c) Length: +/- 5mm | ||||
| Surface | annealing,pickling | |||
| sandblasting | ||||
| Application | industry,exhausting,water | |||
| Test | Squash test, extended test, water pressure test,heat treatment, NDT | |||
| Chemical Composition of Material | Material | 201 | 316L | 304 |
| C | ≤0.15 | ≤0.035 | ≤0.08 | |
| Si | ≤1.00 | ≤1.00 | ≤1.00 | |
| Mn | 5.5-7.5 | 2 | ≤2.00 | |
| P | ≤0.06 | ≤0.045 | ≤0.045 | |
| S | ≤0.03 | ≤0.03 | ≤0.03 | |
| Cr | 16-18 | 16-18 | 18-20 | |
| Ni | 3.5-5.5 | 10-14 | 8-11 | |
| Mechanical Property | Material Item | 201 | 202 | |
| Tensile Strength | ≥535 | ≥520 | ||
| Yield Strength | ≥245 | ≥205 | ||
| Extension | ≥30% | ≥30% | ||
| Hardness (HV) | <253 | <253 | ||
Chemical Composition
| Specification | Grade | Chemical Composition(wt%) | ||||||
| C | Mn | Ni | Cr | Mo | Ti | |||
| ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
| JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
| ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 | |
Properties
| Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S (N/MM2) | T.S (N/MM2) | EL (%) | HRB | Specific Heat (J/g℃) | Modulus of Elasticity (KN/mm2) | ||
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications
316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.
316Ti: Mainly used for industrial components.
|