High reflective and good adhesion ability solder mask for led pcb printing
| Items | Technical features | Notes |
| Color | Blue | |
| Viscosity (25℃) | 10±2dPa﹒s | VT-04F |
| Fineness | ≤5µm | 0 ~25µm Fineness gauge |
| Solid content | 50±5% | |
| Density (25℃) | 1.10 ~1.20 g/ml | |
| Resolution | 50µm (2.0mil) | |
| Adhesion | 100/100 | Laceration experiment |
| Plating resistance | Copper ,Tin ,Nickle and Aurum | Normal plating technics |
| Hardness | ≥2H | Pencil harder |
| Etching | Acidic/Alkaline etching solution | |
| Pre-baking limit | 75℃, 60min | |
| Package | 5.0kg/bucket , 20kg/box | According to customer requirements |
| Shelf time | 6 months since the date of manufacture | Store below 25℃ in dark |
Working procedure
1. Mixing
Mixing a small amount main agent with hardener and stirring thoroughly,then mixing the mixture above with the remanent main agent,add appropriate diluent and stirring 5-10 minutes. The viscosity of ink is adjusted to 120 PS if printed by hand. And it is adjusted to 180 PS if printed by machine.It is adjusted to 200 PS if it is aluminum tamponade .The viscosity of ink mixed above is measured at 25 degrees. Please use the special diluent of our company if the viscosity of ink needs to adjust.
10-15 minutes after stiring uniformly
1) Single side printing separately
First side:72-76 degrees,15-18 min
Second side:72-76 degrees,30-35 min
300-500mJ/cm2,Black ink:600-750mJ/cm2,exposure step:10-12 steps
Developing solution:0.8-1.2wt% Na2CO3 or K2CO3 aqueous solution
Developing solution temperature:28-32 degrees
Spray pressure:1.5-2.5kg/cm2
Developing time:40-90 seconds
Spray Tin board:150 degrees*(60-120min)
Chemical-plating Aurum board:150 degrees*(50-60min)
Thick copper plate,boards printed with black ink should be post-black in subsection:75 degrees*(60-120min)+100 degrees*30 min+150 degrees*(60-90min)
6 months since the date of manufacture,store below 25 degree in dark
1) Mixing the ink fully before using
2) We will offer you special diluent or PMA if the ink need dilute
3) The values above are based on experiments in our lab.Experiments need to be carried out in order to get proper using condition.
Our company:
Hubei Nuojinsen Technology Co.,Ltd ,after years of unremitting efforts,Combined with foreign advanced technology and process,Production of PCB ink has reached the technical level, conforms to the requirement of RoHS environmental protection directive, with excellent quality and excellent service is deeply trusted by customers.
Company passed the ISO9001 quality standard certification and ISO
14000 environment system certification, is the national high and new technology enterprise. Company has
achieved many honors, including: the Chinese photographic society
of professional committee of the radiation curing, deputy director
of the unit,the ninth national committee, deputy director of the
printed circuit branch of unit, the national standardization
technical committee, deputy director of the unit printed circuit
boards, printed circuit industry in China in the second session of
"nation" brand enterprise, Hubei in 2015 advanced units of
ecological construction and environmental protection, etc.Companies
always adhere to the science and technology as the first
productivity. Enterprise technology center in Wuhan city, the
company has built in Wuhan city, and form a complete set of PCB ink
research and development of engineering technology research center,
two platform, and lead to make the printed circuit with marking ink
and the printed circuit using resistance solder "two important
industry standards. The company's flagship product, solder resist
ink (solder mask) series of products have been American UL safety
certification.