Stud Bar ASTM A193 Grade B7 B7M B16 "End to End" Class 2A 1/2"-13 ~ 4"-8 Plain/ Black/ Zinc/ Hdg/ PTFE
Ferritic steels shall be allowed to cool to a temperature below the cooling transformation range immediately after rolling or forging. Bolting materials shall then be uniformly reheated to the proper temperature to refine the grain (a group thus reheated being known as a quenching charge), quenched
TABLE 1 Chemical Requirements (Composition, percent)A
Ferritic Steels
Description | ||||||||||||||||
and UNS | ||||||||||||||||
Grade | Designation | Class | Carbon | Manganese | Phosphorus | Sulfur | Silicon | Chromium | Nickel | Molybdenum | Cooper | NiobiumF | Titanium | Vanadium | Aluminum | Nitrogen |
B5 | 5 % Chromium | 0.10 min | 1.00 | 0.040 | 0.030 | 1.00 | 4.0–6.0 | . . . | 0.40–0.65 | . . . | . . . | . . . | . . . | . . . | . . . | |
Product | ||||||||||||||||
Analysis | 0.01 | 0.03 | 0.005 | 0.005 | 0.05 | 0.10 | . . . | 0.05 | . . . | . . . | . . . | . . . | . . . | . . . | ||
VariationB | ||||||||||||||||
B6, | 12 % | |||||||||||||||
B6X | Chromium | 0.08–0.15 | 1.00 | 0.040 | 0.030 | 1.00 | 11.5–13.5 | . . . | . . . | . . . | . . . | . . . | . . . | . . . | . . . | |
(410), | ||||||||||||||||
S41000 | ||||||||||||||||
Product | ||||||||||||||||
Analysis | 0.01 over | 0.03 | 0.005 | 0.005 | 0.05 | 0.15 | . . . | . . . | . . . | . . . | . . . | . . . | . . . | . . . | ||
VariationB | ||||||||||||||||
B7, | Chromium- | D | ||||||||||||||
B7M | MolybdenumC | 0.38–0.48 | 0.75–1.00 | 0.035 | 0.040 | 0.15–0.35 | 0.80–1.10 | . . . | 0.15–0.25 | . . . | . . . | . . . | . . . | . . . | . . . | |
Product | ||||||||||||||||
Analysis | 0.02 | 0.04 | 0.005 | 0.005 | 0.02 | 0.05 | . . . | 0.02 | . . . | . . . | . . . | . . . | . . . | . . . | ||
VariationB | ||||||||||||||||
B16 | Chromium- | |||||||||||||||
Molybdenum- | 0.36–0.47 | 0.45–0.70 | 0.035 | 0.040 | 0.15–0.35 | 0.80–1.15 | . . . | 0.50–0.65 | . . . | . . . | . . . | 0.25–0.35 | 0.015E | . . . | ||
Vanadium | ||||||||||||||||
Product | ||||||||||||||||
Analysis | 0.02 | 0.03 | 0.005 | 0.005 | 0.02 | 0.05 | . . . | 0.03 | . . . | . . . | . . . | 0.03 | . . . | . . . | ||
VariationB | ||||||||||||||||
Austenitic Steels | ||||||||||||||||
Grade | Description | |||||||||||||||
and UNS | Classes | Carbon | Manganese | Phosphorous | Sulfur | Silicon | Chromium | Nickel | Molybdenum | Copper | NiobiumF | Titanium | Vanadium | Aluminum | Nitrogen | |
Designation | ||||||||||||||||
B8, | 304, S30400 | 1, 1A, 1D, | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 18.0–20.0 | 8.0–11.0 | . . . | . . . | . . . | . . . | . . . | . . . | . . . |
B8A | 2 | |||||||||||||||
Product | ||||||||||||||||
Analysis | 0.01 | 0.04 | 0.010 | 0.005 | 0.05 | 0.20 | 0.15 | . . . | . . . | . . . | . . . | . . . | . . . | . . . | ||
VariationB | ||||||||||||||||
B8C, | 347, | 1, 1A, 1D, | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 17.0–19.0 | 9.0–12.0 | . . . | . . . | 10×C | . . . | . . . | . . . | . . . |
B8CA | S34700 | 2 | to 1.10 | |||||||||||||
Product | 0.05 | |||||||||||||||
Analysis | 0.01 | 0.04 | 0.010 | 0.005 | 0.05 | 0.20 | 0.15 | . . . | . . . | . . . | . . . | . . . | . . . | |||
under | ||||||||||||||||
VariationB | ||||||||||||||||
B8M, | ||||||||||||||||
B8MA, | 316, | 1, 1A, 1D, | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 16.0–18.0 | 10.0–14.0 2.00–3.00 | . . . | . . . | . . . | . . . | . . . | . . . | |
B8M2, | S31600 | 2 | ||||||||||||||
B8M3 | ||||||||||||||||
Product | ||||||||||||||||
Analysis | 0.01 | 0.04 | 0.010 | 0.005 | 0.05 | 0.20 | 0.15 | 0.10 | . . . | . . . | . . . | . . . | . . . | . . . | ||
VariationB |