Stud Bar 975 DIN976 Metric Size B7 B7M B16 "End to End"
Grades 2H, 2HM, 3, 6, 6F, 7, 7M, and 16 nuts shall be hot- or cold-forged or shall be machined from hot-forged, hot-rolled, or cold-drawn bars and shall be heat treated to meet the required mechanical properties. These grades shall be uniformly reheated to the proper austenitizing temperature (a group thus reheated being known as a quenching charge) and quenched under substantially uniform conditions for each quenching charge and tempered as shown below. Grades 2H, 2HM, 3, 7, and 7M shall be liquid quenched. Grades 6 and 6F shall be quenched in liquid or inert gas. Grade 16 shall be heated to a temperature range from 1700 to 1750 °F (925 to 955 °C) and oil quenched.
Minimum Tempering Temperature, °F | |
Grade | [°C] |
2H | 850 [455] |
2HM | 1150 [620] |
3 | 1050 [565] |
6 and 6F | 1100 [595] |
7 | 1100 [595] |
7M | 1150 [620] |
16 | 1200 [650] |
Nuts machined from bar heat treated in accordance with this specification need not be reheat-treated. For Grade 2HM and 7M nuts, a final stress relief shall be done at or above the minimum tempering temperature after all forming, machining, and tapping operations. This final stress relief may be the tempering operation.
Grade 6 and 6F nuts shall be tempered for a minimum of 1 h at the temperature.
Grades 8, 8C, 8CLN, 8M, 8T, 8F, 8P, 8N, 8MN, 8R, 8S, 8LN, 8MLN, 8MLCuN, 8ML4CuN, and 9C nuts shall be hot or cold forged, or shall be machined from hot-forged, hot-rolled or cold-drawn bars.
Grades 8A, 8CA, 8CLNA, 8MA, 8TA, 8FA, 8PA, 8NA, 8MNA, 8RA, 8SA, 8LNA, 8MLNA, 8MLCuNA, 8ML4CuNA, and 9CA nuts shall be hot- or cold-forged or shall be machined from hot-forged, hot-rolled, or cold-drawn bars and the nuts shall subsequently be carbide-solution treated by
heating them for a sufficient time at a temperature to dissolve chromium carbides followed by cooling at a rate sufficient to prevent reprecipitation of the carbides.
Product Name | Threaded rod / Threaded Bar ASTM A193 B7 / B7M "End to End" Class 2A |
Size | Diameter : 1/2"-13 ~ 4"-8; Length : 5mm-5000mm Normal:12ft /3660mm |
Standard | DIN,ISO,ASME/ANSI,ASTM,BS,JIS,CNS,AS,EN,GOST,IFI and Non-standard |
| |
Finishing | Plain, Black,Yellow/White Zinc Plated,H.D.G, PTFE 1424 |
Grade | DIN: Gr 4.8, 8.8 ,10.9, 12.9 ; SAE: Gr2, 5, 8 ; ASTM:193-2020 194-2020 320-2022 |
Material40 | 40CrMo, Alloy Steel , Stainless Steel , Brass,Carbon Steel |
Thread Type | UNC, UNF, UNEF, M, BSW, BSF, TR, ACME, NPT |
Production Technique | Cold forging, Hot forming, Chanfer,Marking,Maching, Heat Treatment ,ect |
Production Capacity | 1000 tons per Month |
Packaging | Bundles,Gross Weight about 25kgs per carton then 36 cartons per pallet or as customer's requirments |
Certificate | ISO9001; API; 3.1.B |
Trade Terms | FOB , CIF, CNF,CFR,EXW |
Terms of Payment | T/T, L/C , Western Union , Paypal , Money Gram |
Delivery Time | Within 30days |