| Grade : | X6CrNiMoTi17-12-2 | ||||||||||||||||
| Number: | 1.4571 | ||||||||||||||||
| Classification: | Austenitic stainless steel | ||||||||||||||||
| Density: | 8 g/cm ³ | ||||||||||||||||
| Standard: |
|
1.4571 Steel Plate flange Chemical composition % of steel X6CrNiMoTi17-12-2 (1.4571): EN 10088-2-2005
| Ti = 5 * C to 0.7 Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended. Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. |
| C | Si | Mn | Ni | P | S | Cr | Mo | Ti |
| max 0.08 | max 1 | max 2 | 10.5 - 13.5 | max 0.045 | max 0.015 | 16.5 - 18.5 | 2 - 2.5 | max 0.7 |
1.4571 Steel Plate flange Mechanical properties of steel X6CrNiMoTi17-12-2 (1.4571)
| Rm - Tensile strength (MPa) (+A) | 500-700 |
| Rm - Tensile strength (MPa) (+AT) | 500-730 |
| Rm - Tensile strength (MPa) (+AT+C) | 810-850 |
| Rp0.2 0.2% proof strength (MPa) (+A) | 200-240 |
| Rp0.2 0.2% proof strength (MPa) (+AT) | 190-210 |
| KV - Impact energy (J) transverse, (+A) | +20° 60 | -196° 60 |
| KV - Impact energy (J) longitud., (+A) | +20° 100 |
| A - Min. elongation at fracture (%) (+A) | 30-40 |
| A - Min. elongation at fracture (%) longitud., (+AT) | 35-45 |
| Nominal diameter (mm): | 2 - 50 |
| Z - Reduction in cross section on fracture (%) | 60-65 |
| Brinell hardness (HB): (+A) | 215 |
| Brinell hardness (HB): (+AT) | 210 |