SUS 317 TP317L stainless welded pipe Sch5S-160S For High Temperature Service
Finish and repair:
The surface of the welded stainless steel tube must be clean and
free of scale and contaminating iron particles. It can be bright
annealed but may be pickled, blasted or can be passivated.
Repair by welding. Permitted on <−20% of the weld seam length of
welded stainless steel tube if >−NPS 6 and having a wall
thickness >−0.200 in (mm). Tungsten-arc welding process is used
for repairs, with filler metal to a grade as specified in A 312
(not repeated here). Weld repairs must be identified on the pipe
and in test certificate.
Pipe Specifications - ASTM A312/A312M: welded austenitic stainless steel pipes.
This specification covers austenitic steel pipe intended for high
temperature and general corrosive service.
H grades in the chemical composition table are specifically for
high temperature service.
Grade: Austenite,Ferritic, Super-Ferritic, Duplex Stainless Steel
Standard:ASTM A249/A213/A269/A554/A270/A312/A268/A778/A789/A790
DIN11850/17456/17458/SMS/ISO2037/ISO1127/EN10217-7 EN10216
OD:3.175-1016mm,WT: 0.5-20mm,Length:1000-20000mm,Type: Seamless, Welded
Manufacture:
In order to comply with this specification welded stainless steel
tube must be manufactured by an automatic welding process using no
filler metal, or it must be a seamless pipe. If a welded stainless
steel tube has a nominal pipe size greater than 14'' then it may be
constructed from two longitudinal sections, and hence have two
longitudinal welds. The pipe may be either hot finished or cold
finished.
Mechnical Propertiies:
| Grade | UNS Designation | Tensile Strength, min ksi [Mpa] | Yield Strength, min ksi [Mpa] |
|---|---|---|---|
| TP304 | S30400 | 75 [515] | 30 [205] |
| TP304L | S30403 | 70 [485] | 25 [170] |
| TP304H | S30409 | 75 [515] | 30 [205] |
| TP316 | S31600 | 75 [515] | 30 [205] |
| TP316L | S31603 | 70 [485] | 25 [170] |
| TP316H | S31609 | 75 [515] | 30 [205] |
| TP310S | S31008 | 75 [515] | 30 [205] |
| TP310H | S31009 | 75 [515] | 30 [205] |
| TP321 | S32100 | 75 [515] | 30 [205] |
| TP321H | S32109 | 75 [515] | 30 [205] |
| TP347 | S34700 | 75 [515] | 30 [205] |
| TP347H | S34709 | 75 [515] | 30 [205] |
1. Heat Exchangers, Condensers & Pressure Vessels
2. Chemical & Petrochemical
3. Gas Industry
4. Power Generation
5. Pressure Vessels
6. Marine Equipments
7. Food & Beverage Processing
8. Automotive
9. Pulp & Paper
Specifications:
| NPS | ASTM A312 OD Tolerance | |||
| + | - | |||
| inch | mm | inch | mm | |
| 1/8~1 1 / 2 >1 1 / 2 ~4 >4~8 >8~18 >18~26 >26~34 >34~48 | 1/64(0.015) 1/32(0.031) 1/16(0.062) 3/32(0.093) 1/8(0.125) 5/32(0.15 | |||
| NPS | ASTM A312 WT Tolerance ,% | |
| + | - | |
| 1/8-2 1 /2 | 20.0 | 12.5 |
| 3~18,t/D≤5% | 22.5 | 12.5 |
| 3~18,t/D>5% | 15.0 | 12.5 |
| ≥20, welded | 17.5 | 12.5 |
| ≥20, seamless,t/D≤5% | 22.5 | 12.5 |
| ≥20,seamless,t/D>5% | 15.0 | 12.5 |