ASTM B209 5052 H34 T3 Aluminum Sheet Price For Marine Grade
ASTM B209 5052 H34 T3 Aluminum has excellent finishing qualities and anodized coatings are bright and clear. Weldability is very good and 5052 has good resistance to corrosion, especially in salt-water / marine atmospheres.
ALLOY DESIGNATIONS
Aluminium alloy EN AW 5052 has similarities to the following standard designations and specifications ;
Alloy 5052 UNS A95052, ASTM B209
DIN AlMg2.5
PROPERTIES OF 5052 H34 ALUMINUM
Alloy QQ-A-250/8, 5052 is supplied in a wide range of tempers:
O - Soft
H34 - Stabilised - A low temperature thermal treatment or heat introduced during manufacture which stabilises the mechanical properties and relieves residual internal stress, plus usually improves ductility
H112 - Alloys that have some tempering from shaping but do not have special control over the amount of work-hardening or thermal treatment.
H24 - Work hardened by rolling then annealed to half hard
H26 - Work hardened by rolling then annealed to three-quarter hard
H32 - Work hardened by rolling then stabilised by low-temperature heat treatment to quarter hard
T36 - Solution heat treated then cold worked by a reduction of 6%
5052 H34 ALUMINUM DATA SHEET
| Chemical Properties | % Value |
| Silicon (Si) | 0,00 - 0,25 |
| Chromium (Cr) | 0,15 - 0,35 |
| Manganese (Mn) | 0,00 - 0,10 |
| Magnesium (Mg) | 2,20 - 2,80 |
| Copper (Cu) | 0,00 - 0,10 |
| Iron (Fe) | 0,00 - 0,40 |
| Zinc (Zn) | 0,00 - 0,10 |
| Aluminium (Al) | Balance |
| Physical Properties | Value |
| Density | 2.68 g/cm³ |
| Melting Point | 607 °C |
| Thermal Expansion | 23.8 x10^-6 /K |
| Modulus of Elasticity | 70 GPa |
| Thermal Conductivity | 140 W/m.K |
| Electrical Resistivity | %35 IACS |
| Mechanical Properties | Value |
| Proof Strength | 210 MPa |
| Yield Strength | 260 MPa |
| Shear Strength | 145 MPa |
| Elongation A50 mm | %11 |
| Modulus of Elasticity | 70 GPa |