Tai\'an Wantong Composite Material Co., Ltd. |
Verified Suppliers
|
|
Property |
Value | ||||||||||||
0.75mm | 1.00mm | 1.25mm | 1.5mm | 2.00mm | 2.50mm | 3.00mm | |||||||
Density G/CM3 |
0.939 | ||||||||||||
Tensile properties | |||||||||||||
Strength at yield, N/mm | 11 | 15 | 18 | 22 | 29 | 37 | 44 | ||||||
Break at yield, N/mm | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||||||
Elongation at yield, % |
12 | ||||||||||||
Elongation at break, % |
700 | ||||||||||||
Right angle tear strength, N | 93 | 125 | 156 | 187 | 249 | 311 | 374 | ||||||
Puncture strength, N | 240 | 320 | 400 | 480 | 640 | 800 | 960 | ||||||
Stress crack resistance using notched constant tensile load, H |
300 | ||||||||||||
Carbon Black Content of a % |
2.0-3.0 | ||||||||||||
Standard OIT,MIN; or |
100 | ||||||||||||
Pressure OIT,MIN |
400 | ||||||||||||
Baking 90D later, Reserved standard OIT %; or |
55 | ||||||||||||
Baking 90D later, Reserved Pressure OIT% |
80 | ||||||||||||
Irradiate with UVA after 1600H,Reserved Standard OIT%;or |
50 | ||||||||||||
Irradiate with UVA after 1600H,Reserved pressure OIT% |
50 | ||||||||||||
’-70°C Embrittlement of low-temperature impact |
Passed | ||||||||||||
coefficient of permeability of water steam G.CM/(CM2.S.PA) |
≤1.0*10-13 | ||||||||||||
Dimensional Stability (%) |
±2 |