China Hot rolled 3mm stainless steel rod stock 310S 321 304
It has high strength, good low-temperature impact toughness, and a typical tensile strength of 900 -1200 N/mm2. 1.7225 steel has better performance than 34CrMo4 steel due to its higher carbon and chromium content. Similar to AISI 4140, there is little difference in Mn and Cr content. The material also has good workability and good wear resistance, but the temper brittleness is not obvious, and the weldability is poor. It can be used for static and dynamic stressed parts of vehicles, engines and machines. For parts with larger cross-sections, crankshafts, gears. It can also produce mining spare parts, induction hardening pins, fastener accessories, oil and gas drilling equipment. |
| Commodity Description | |
| 1. Name of product | Stainless steel bar |
| 2. Diameter: | 3-300mm |
| 3. Shape: | Round, hexangular, square |
| 4. Standard: | ASTM, AISI, JIS, GB, DIN, etc. |
| 5. Material: | 201, 304, 304L, 316, 316L, 321, 309S, 310S, 904L |
| 6. Surface: | Bright, black |
| 7. Technique: | Cold/Hot Rolled |
| 8. Certification: | ISO |
| 9. Packing: | Standard export package or as your request |
| 10. Application: | Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, etc. |
| 11. Advantages: | 1. Corrosion resistance. 2. High temprature resistance. 3. High production ability. 4. Reasonable price. 5. Excellent quality. 6. Various size. |
| 12. Main Market: | North America, South America, Europe, Southeast Asia, Africa, Oceania, Middle East, Eastern Asia, Central America |
| 13. MOQ; | 2 Metric Tons |
| 14. Delivery Time: | Within 7-30 working days |
| 15. Payment: | T/T, L/C, Western union |
Chemical Composition
| Specification | Grade | Chemical Composition(wt%) | ||||||
| C | Mn | Ni | Cr | Mo | Ti | |||
| ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
| JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
| ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 | |
Properties
| Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S | T.S | EL | HRB | Specific Heat | Modulus of Elasticity (KN/mm2) | ||
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |