ASTM 50mm Solid Round Bar Hot Rolled S235 Carbon Steel Q235B ST37 S235JR
Carbon steels are a series of alloys of carbon and iron containing up to about 1% carbon and up to 1.65% Mn, with elements added in specific quantities for deoxidization and residual quantities of other elements. |
PRODUCT DESCRIPTION
| Product Name | Hot rolled MS Carbon steel Alloy steel round bar cheap price | |
| Material | ASTM | 1005,1006,1008,1010,1015,1020,1025,1030,1035,1040,1045, 1050,1055,1060,1065,1070,1080,1084,1016,1022 |
| DIN | Ck10,Ck15,Ck22,Ck25,Ck30,Ck35,Ck40,Ck45,Ck50, 30Mn4,40Mn4 | |
| BS | 040A04,095M15,045M10,080A40,045M10,080M50 | |
| GB | Q195, Q235,Q345 | |
| Standard | GB/T799,ASTM A29,A108,A321,A575,BS970,DIN1652,JIS G4051 | |
| Surface | Black painted,galvanized | |
| Specifications | Round bar | 8mm~800mm |
| Angle bar | 3mm*20mm*20mm~12mm*800mm*800mm | |
| Square bar | 4mm*4mm~100mm*100mm | |
| Flat bar | 2*10mm~100*500 | |
| Hexagonal | 4mm~800mm | |
| Length | 2m,4m,5.8m,6m,11.8m,12m or as required. | |
Chemical Composition
| Grade | C≤ | Mn | P≤ | S≤ | Si≥ | Cr≤ | Cu≤ | Mo≤ | Ni≤ | V≤ |
| A | 0.25 | 0.27-0.93 | 0.035 | 0.035 | 0.10 | 0.40 | 0.40 | 0.15 | 0.40 | 0.08 |
| B | 0.30 | 0.29-1.06 | 0.035 | 0.035 | 0.10 | 0.40 | 0.40 | 0.15 | 0.40 | 0.08 |
| C | 0.35 | 0.29-1.06 | 0.035 | 0.035 | 0.10 | 0.40 | 0.40 | 0.15 | 0.40 | 0.08 |
Properties
| Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S (N/MM2) | T.S (N/MM2) | EL (%) | HRB | Specific Heat (J/g℃) | Modulus of Elasticity (KN/mm2) | ||
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications:316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.316Ti: Mainly used for industrial components. |