DIN X38CrMoV5-1 Alloy Steel Plate Corrosion Resistant Good Machinability

Designation by Standards

Mat. No.	DIN	EN	AISI
1.2343	X38CrMoV5-1	X27CrMoV51	H11

Chemical Composition (in weight %)

C	Si	Mn	Cr	Mo	Ni	V	W	Others
0.37	1.0	0.38	5.15	1.30	-	0.40	-	-

Description
H11 is one of the Hot Work, Chromium type tool steels. It is relatively low in carbon content and has good toughness and deep hardens by air quench from heat treatment. Good combination of toughness, hardness and wear resistance in hot. Resistance to softening and to cracking.

Applications
H11 is often used for highly stressed structural parts such as aircraft landing gear. It resists softening at temperatures up to 537^oC while retaining good ductility and toughness even at strength levels on the order of 275 ksi. Tools for hot forging of light metal. Pressure die casting tools. Dies, mandrels, punchers, knives, moulds. This grade can be water cooled. For most highest requirements we recommended UTOPMO1 EFS.

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [10³ x N/mm²]: 215, 176 (at 500^oC), 165 (at 600^oC)
Density [g/cm³]: 7.80, 7.64 (at 500^oC), 7.60 (at 600^oC)
Thermal conductivity [W/m.K]: 25, 28.5 (at 500^oC), 29.3 (at 600^oC)
Electric resistivity [Ohm mm²/m]: 0.52, 0.86 (at 500^oC), 0.96 (at 600^oC)
Specific heat capacity[J/g.K]: 0.46, 0.55 (at 500^oC), 0.59 (at 600^oC)

Coefficient of Linear Thermal Expansion 10^{-6 o}C^-1

20-100oC	20-200oC	20-300oC	20-400oC	20-500oC	20-600oC	20-700oC	20-700oC
9.8	12.5	13.0	13.2	13.5	13.7	13.8	14.0

Continuous Cooling Transformation (CCT) Diagram

Click the image to enlarge the diagram.

Soft Annealing
Heat to 800-840^oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 229.

Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650^oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Hardening
Harden from a temperature of 1000-1040^oC followed by air, oil quenching or warm bath quenching 500-550^oC. Hardness after quenching is 50-56 HRC.

Tempering
Tempering temperature: See the data bellow.

Tempering Temperature (^oC) vs. Hardness (HRC)

100oC	200oC	300oC	400oC	500oC	550oC	600oC	650oC	700oC
53	52	52	52	54	52	48	38	30
1845	1790	1790	1790	1910	1790	1570	1200	970

Tempering Diagram

Click the image to enlarge the diagram.

Diagram Tempering Temperature – Mechanical Properties

Click the image to enlarge the diagram.

Diagram Tempering Temperature – Mechanical Properties

Click the image to enlarge the diagram.

Forging
Hot forming temperature: 1100-900^oC.

Cold Working
Cold working may readily be accomplished on H11 by conventional methods.

Machinability
Machinability is reasonably good, approximately 75% that of the W group water hardening low alloy tool steels.

Corrosion Resistance
This is a steel alloy and not corrosion resistant. It will rust unless protected.

Welding
H11 is a readily weldable alloy by conventional methods.

Forms manufactured: Please see the Dimensional Sales Program.

Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.