904L Hot Rolled 8mm Stainless Steel Sheet Plate Ss 304 316 321 310S 200mm

Country/Region	china
City & Province	wuxi shandong

Product Details

904L Hot Rolled 8mm Stainless Steel Sheet Plate Ss 304 316 321 310S 200mm

Like 316L, 904L stainless steel is a low-carbon austenitic stainless steel. However, its chemical composition includes greater numbers of chromium (19-23%) and molybdenum (4-5%), which gives the alloy greater corrosion resistance than 316L.

Is 316L better than 904L?

Type 904L contains more chromium, molybdenum and nickel then 316L, plus also some copper, manganese and silicon, which makes it more corrosion resistant than 316L. But the main issue with 904L, besides its extremely high price, is that it is still harder to process than 316L.

Specification

Stainless Steel 904l Grade Plate Thickness	0.3 to 1200 mm or as required
SS 904l Grade Plate Process	Hot/ Cold Rolled
Type	Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate
904l Stainless Steel Plate Length	0-12mm or as required
904l SS Plate Width	0-2500mm or as required
Test	TUV, SGS testing, UT etc
AISI 904l Stainless Steel Plate surface	No.1, No. 2D, No. 2B, BA, No.3, No.4, hairline, No.6, No.7, 2B, 2D, BA NO(8), Hot rolled plate (HR), SATIN, No.1 finish hot rolled, Cold rolled sheet (CR), 1D, brush, mirror etc.

Chemical composition

Grade	C	Mn	Si	P	S	Cr	Mo	Ni	Cu
SS 904L	0.020 max	2 max	1.00 max	0.040 max	0.030 max	19.00 – 23.00	4.00 – 5.00 max	23.00 – 28.00	1.00 – 2.00

Mechanical Properties

Density	Melting Point	Tensile Strength	Yield Strength (0.2%Offset)	Elongation
7.95 g/cm3	1350 °C (2460 °F)	Psi – 71000 , MPa – 490	Psi – 32000 , MPa – 220	35 %

physical properties

Grade		904L
Density (kg/m3)		7900
Elastic Modulus (GPa)		190
Mean Co-eff of Thermal Expansion (µm/m/°C)	0-100°C	15
	0-315°C
	0-538°C
Thermal Conductivity (W/m.K)	At 20°C	11.5
	At 500°C
Specific Heat 0-100°C (J/kg.K)		500
Elec Resistivity (nΩ.m)		952

Most Commonly Used ASTM B625 UNS N08904 Sheet Types

904L Stainless Steel Sheet

904L Stainless Steel Plate

SS 904L Plate

astm a240 type 904l Sheet

ASTM B625 UNS N08904 Plate

DIN 1.4539 sheet

Why Choose Us?

1. who are we?
We are based in wuxi, China, sell to Domestic Market and Abroad Market. There are total about 51-100 people in our office.

2. how can we guarantee quality?
Always a pre-production sample before mass production; Always final Inspection before shipment;

3.what can you buy from us?
stainless steel plate,stainless steel coil,stainless steel sheet,stainless steel pipe and tube,sainless steel bar and other metal.

4. why should you buy from us not from other suppliers?
Runs perennial exports of quality assured steel mills ,including Shanxi TISCO, Baosteel, Shanghai Krupp, Ningbo Baoxin, Guangzhou Lianzhong, Zhangjiagang Pohang, Qingdao Pohang, Sweden AvestaPolarit, Finland OUTKUMPU, Spain Acerinox, South Africa Columbus