1.4835 DIN X9CrNiSiNCe 21-11-2 Stainless Steel Flat Bar F45 UNS S30815 Plates

Country/Region	china
City & Province	mianyang

Product Details

1.4835 DIN X9CrNiSiNCe 21-11-2 Stainless Steel Flat Bar F45 UNS S30815 Plates

Product Information

X9CrNiSiNCe 21-11-2/1.4835 is a heat-resistant austenitic stainless steel. Its chemical composition is balanced, so that it has the most suitable comprehensive performance in the temperature range of 850 ° C to 1100 ° C. It has extremely high oxidation resistance and creep resistance. Deformation and creep rupture strength; good high temperature corrosion resistance in most gaseous media, good formability and weldability, and sufficient machinability.

Size Range

Round bar / Wire rod (Diameter): 10.0 mm to 500 mm

Square bar / Flat bar: 5.0 mm to 500 mm

Forging piece: Stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.

Heavy/middle plate via hot rolled: T5 - 1000 mm X W10 - 1000 mm X L800-12000 mm

Sheet steel via cold rolled: T8.0 - 10 mm X W10 - 1000 mm X L100 - 1000 mm

Steel strip via cold rolled: T10 - 10 mm X W5 - 1000 mm X L (or in coil form)

Length: Fixed length or random length or based on the customer's special requirement.

Chemical Composition and standard

X9CrNiSiNCe 21-11-2 / 1.4835

S30815 / F 45

X7CrNiSiNCe21-11

4835-308-15-U

DIN EN 10095-2018

ASTM A182/A182M-2018

ISO 15510-2014

C(％): 0.05~0.12
Si(％): 1.4~2.5
Mn(％): ≤1.0
P(％)≤: 0.045
S(％)≤: 0.015
Cr(％): 20~22
Ni(％): 10~12

Mo(%): -

N(%): 0.12~0.20

Ce(%): 0.03~0.08

C(％): 0.05~0.10
Si(％): 1.4~2.0
Mn(％): ≤0.8
P(％)≤: 0.04
S(％)≤: 0.03
Cr(％): 20~22
Ni(％): 10~12

Mo(%): -

N(%): 0.12~0.20

Ce(%): 0.03~0.08

C(％): 0.05~0.10
Si(％): 1.4~2.0
Mn(％): ≤0.8
P(％)≤: 0.040
S(％)≤: 0.030
Cr(％): 20~22
Ni(％): 10~12

Mo(%): -

N(%): 0.14~0.20

Ce(%): 0.03~0.08

X9CrNiSiNCe 21-11-2 / 1.4835 Mechanical Properties (+AT)

Tensile strength,Rm/MPa: 650~850

Yield strength,Rp/MPa: ≥310

Elongation/%: Thickness 0.5~3mm: ≥13

Thickness ≥3mm: ≥15

Reduction of area, ψ/%: --

Impact, KV /J: --

Hardness/ HB: ≤210

Applications

X9CrNiSiNCe 21-11-2 W-Nr 1.4835 Applied to boiler equipment, steelmaking, furnace and continuous casting equipment, mining equipment and cement production equipment, etc.