stainless steel 304 316 316L M8 Stud Bolt Double End All Thread Rod
Description:
ASTM A193 B7 B7M A320 L7 L7M Stud Bolt threaded rod are commonly used in offshore flatform, oil and gas. With PTFE coating, it is in high anti-corrosion.
The specification for ASTM A193 covers alloy and stainless steel bolting for pressure vessels, valves, flanges, and fittings for high temperature or high pressure service, low temperature, or other special purpose applications. The ASTM A193 specification covers bars, bolts, screws, studs, stud bolts, and wire. The material may be further processed by centerless grinding or by cold drawing. Below are some of the ASTM A193 grades used commonly.
Common ASTM A193 specifications:
ASTM A193 B7 Alloy steel, AISI 4140 or 4142, quenched and tempered
ASTM A193 B6 Stainless steel, AISI 410, heat treated
ASTM A193 B8 Class 1 Stainless steel, AISI 304, carbide solution treated.
ASTM A193 B8M Class 1 Stainless steel, AISI 316, carbide solution treated.
ASTM A193 B8 Class 2 Stainless steel, AISI 304, carbide solution treated, strain hardened
ASTM A193 B8M Class 2 Stainless steel, AISI 316, carbide solution treated, strain hardened
ASTM A193 B8T Class 1 or 2 Stainless steel, AISI 321, with additional element of Titanium
ASTM A193 B16 Chromium-Molybdenum-Vanadium, similar to B7 with Vandium added
ASTM A193 B7M Similar properties as B7 but with specialized heat treating to create differing mechanical properties
ASTM A193 B8R Stainless steel, AISI 209, also known as Nitronic 50, nitrogen strengthened
ASTM A193 B8S Stainless Steel, AISI 218, also known as Nitronic 60, nirtrogen strengthened
| Chemical Composition | ||||||||||||
| Grade L7M | C(%) | Si(%) | Mn(%) | P≤(%) | S≤(%) | Cr(%) | Mo(%) | |||||
| Requirement Standard | 0.37-0.49 | 0.15-0.35 | 0.65-1.10 | 0.035 | 0.04 | 0.75-1.20 | 0.15-0.25 | |||||
| Test results | 0.39 | 0.21 | 0.82 | 0.012 | 0.01 | 0.97 | 0.19 | |||||
| Heat No. | 15706761 | |||||||||||
| ITEM NO. POSITION | IMPACT TEST(-73℃) (10mmX10mmX55mm) | Average value of AKV≥27J,And 1result ≥20J is pemitted | TESTING RESULTS:29/32/31 Average value :30.7J It's pass | |||||||||
| 1 | 3"-8UNCx24.5" | |||||||||||
| Mechanical property | ||||||||||||
| Machined sample | Test HRB 99 | |||||||||||
| Tensile Strength(Stress)ob≥690Mpa | Yield Strength(Stress) oS≥552MPa | Contraction Ψ≥50% | Elongation s≥16% | |||||||||
| 860 | 780 | 62 | 21 | 95/97/97 | ||||||||
| JUDGEMENT | PASS | |||||||||||
| Name: (Maichuan) | stainless steel 304 316 316L M8 Stud Bolt Double End All Thread Rod |
| Equal Standard | DIN975 DIN976 ASTM A193 ASTM A320 |
| Standard No | ASTM A193 ASTM A320 |
| Thread Type | UNC, UNF, UNEF, M, BSW, BSF, TR, ACME, NPT TP |
| Material | Alloy Steel(40Cr/35CrMo/4140) |
| Dimension | Metric size from 6mm-100mm, Inch size from 1/8"-3-1/2". |
| Surface treatment | PTFE, PTFE, Xylan Blue, treatment: Plain, black finished, Zinc plated (Galv), Hot DIP Galvanized, Nickel, phosphate black, DACRO coating, etc. |
| Production Technique | Cold forging, Hot forming, Machining, Heat treatment, Staming, etc |
| Grade | ASTM A193 B7 B7M A320 L7 L7M |
| Tolerance | 6g |
Application:
Oil and Gas.
Advantages:
1. Specialized in manufacturing electric power fittings.
2. Rich manufacture experience.
3. High quality with competitive price.
4. Domestic and Overseas markets.
5. Well equipped with complete facilities.
6. Strict quality control and excellent after-sales service.