310S stainless steel plate is an austenitic stainless steel used in high temperature applications. It is used in temperatures up to 2,100℉ in continuous service. This grade contains 25% chromium and 20% nickel, making it highly resistant to oxidation and corrosion. 310S stainless steel is the lower carbon version of 310 plate which is less prone to embrittlement and sensitization in service. 310H stainless steel plate is the high carbon version. They are widely used in moderately carburizing atmospheres, as encountered in petrochemical environments. These grades are not recommended for frequent liquid quenching as it suffers from thermal shock. It is often used in cryogenic applications, due to its toughness and low magnetic permeability.
Product Description:
Product Name | Stainless Steel Sheets/Plates Grade 310S |
Size | as required |
Width | 1000mm,1219mm,1500mm or required |
Thickness | 0.1mm～159mm or as required |
Standard | ASTM,UNS,JIS,GB,AS |
Technique | Hot rolled / cold rolled |
Surface Treatment | 2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, chequered, embossed, hairline, sand blast, Brush, etching, Hot rolled plate (HR), Cold rolled sheet (CR), SATIN (Met with Plastic Coated) etc |
Thickness Tolerance | ±0.01mm~ ±0.25mm |
Material | 310S stainless steel |
Application | Petroleum, electronics, chemical industry, medicine, light textile, food, machinery, construction, nuclear power, aerospace, military industry and other industries. |
MOQ | 1 ton , We can accept sample order. |
Shipment Time | Within 15-20 workdays after receiving deposit or workable L/C |
Export Packing | Waterproof paper, and steel strip packed. |
Capacity | 250,000 tons/year |
Chemical Composition:
Weight % (all values are maximum unless a range is otherwise indicated)
| Grade | 310 | 310S | 310H |
| C | 0.25 | 0.08 | 0.40 min. - 0.10 max. |
| Si | 1.5 | 1.5 | 0.75 |
| Mn | 2.0 | 2.0 | 2.0 |
| Cr | 24.0 min.-26.0 max. | 24.0 min.-26.0 max. | 24.0 min.-26.0 max. |
| Ni | 19.0 min.-22.0 max. | 19.0 min.-22.0 max. | 19.0 min.-22.0 max. |
| P | 0.045 | 0.045 | 0.045 |
| S | 0.03 | 0.03 | 0.03 |
Physical Properties :
| Density | Thermal Conductivity 212°F (100°C) |
| 0.285 lbs/in3 | 8.0 BTU/hr/ft2/ft/°F |
| 7.89 g/cm3 | 10.8 W/m-°K |
| Specific Heat | Melting Range |
| 0.12 BTU/lb-°F (32 – 212°F) | 2470 – 2555°F |
| 502 J/kg-°K (0 – 100°C) | 1354 – 1402°C |
| Modulus of Elasticity | Electrical Resistivity |
| 28.5 x 106 psi | 30.7 Microhm-in at 68°C |
| 196 GPa | 78.0 Microhm-cm at 20°C |
Typical Values at 68°F (20°C)
| Yield Strength | Ultimate Tensile | Elongation | Hardness | ||
| 0.2% Offset | Strength | in 2 in. | |||
| psi (min.) | (MPa) | psi (min.) | (MPa) | % (min.) | (max.) |
| 35,000 | 245 | 80,000 | 550 | 45 | 217 Brinell |
Specifications:
| 310 | 310S | 310H |
| UNS S31000 | UNS S31008 | UNS S31009 |
| ASTM A240 | ASTM A240 | ASTM A240 |
| ASTM A480 | ASTM A480 | ASTM A480 |
| ASME SA240 | ASME SA240 | ASME SA240 |
| AMS 5521 | AMS 5521 | AMS 5521 |
Difference between 310 and 310S:
310 stainless steel has a relatively high carbon content of 0.25%, while 310S stainless steel has a low carbon content of 0.08%, and other chemical components are exactly the same. Therefore, 310 stainless steel has higher strength and hardness and poor corrosion resistance. 310S stainless steel has better corrosion resistance and slightly lower strength. 310S stainless steel is difficult to smelt due to its low carbon content, so the price is relatively higher.
FAQ:
Q1. What are your company's main products ?
A1: Our main products are stainless steel plate/sheet, coil, round/square pipe, bar, channel, etc.
Q2. How do you control quality ?
A2: Mill Test Certification is supplied with shipment, Third Party Inspection is available. and we also get ISO,SGS,Alibaba Verified.
Q3. What are the advantages of your company ?
A35: We have many professionals, technical personnel, more competitive prices and best after-dales service than other stainless steel companies.
Q4: What is the terms of packing?
A3: generally, we pack our goods in bundles or coils with rods or belts, we could also pack the goods as the customers requirement.
Q5:What is your delivery time?
A4: For stocks, we could transport the goods to loading port within 7 days after we received your deposit
For production period, it usually takes about 15 days-30 days after receiving the deposit.
Q6. Can you provide sample ?
A7: We can provide the samll samples in stock for free, as long as you contact us.
Customized samples will take about 5-7days.
Q7. How many coutries you already exported ?
A6: Exported to more than 50 countries mainly from America, Russia, UK, Kuwait, Egypt, Turkey, Jordan,India, etc.