Hastelloy C-4 N06455/W.Nr.2.4610 NiMo16Cr16Ti Seamless Tube or Welded Pipe
Hastelloy C-4 is a nickel-chromium-molybdenum alloy with outstanding high temperature stability. It has high ductility and corrosion resistance. It’s high temperature resistance up to 1900 °F (1038 °C) makes it suitable for most chemical process applications in the as-welded condition.
Hastelloy C4 has excellent stability at high temperatures, good ductility and corrosion resistance.It retains its characteristics even after aging up to 1200oF to 1900oF or 649oC to 1038oC. Alloy C-4 offers resistance to grain development precipitation in the welding area so it is highly suitable for the chemical processes in the welding condition. It offers extremely high resistance to stress corrosion cracking and oxidizing conditions up to 1900oF or 1038oC. Hastelloy C-4 offers resistance to mineral acids, organic and inorganic acids, sea water and brine solutions. It has service temperature up to 1900oF or 1038oC. Outstanding resistance to high temperature corrosion and stress corrosion cracking. Great material for use in chemical processing plants and nuclear fuel processing.
Common Trade Names:
Hastelloy C4 , Nicrofer 6616,UNS N06455 , W.Nr:2.4610
Hastelloy C4 Characteristic:
Resistance to Pitting Crevice Corrosion:
HASTELLOY C-4 alloy exhibits high resistance to chloride-induced
pitting and crevice attack, forms of corrosion to which the
austenitic stainless steels are particularly prone. To assess the
resistance of alloys to pitting and crevice attack, it is customary
to measure their Critical Pitting Temperatures and Critical Crevice
Temperatures in acidified 6 wt.% ferric chloride, in accordance
with the procedures defined in ASTM Standard G 48. These values
represent the lowest temperatures at which pitting and crevice
attack are encountered in this solution, within 72 hours.
Hastelloy C4 Applications:
Hastelloy C4 Available Shape:
Grade | UNS | Density | Tensile Strength (MPa min) | Yield Strength (MPa min) | Reduction of Area min (%) | Elongation min (%) | Hardness (HRC) |
HASTELLOY C-4 | N06455 | 8.64 | 690MPa min | 276MPa min | / | 40% min | / |
Chemical Composition(%):
Ni | Cr | Fe | Co | Ti | C | Mo |
Remainder | 14.0-18.0 | 3.0Max | 2.0max | 0.7max | 0.015max | 14.0-17.0 |
Mn | Si | S | P | |||
1.0max | 0.08max | 0.3max | 0.04max |