Injection Molded Epoxy Coated Bonded Neodymium Magnets
About Compression Bonded Magnets
Advantages Of Compression Bonded Magnets
1: Higher magnetic strength than injection molded magnet.
2: High corrosion resistance (Epoxy coating, parylene coating) and temperature resistance, the salt spray teasting >72 hours
3: Magnetizing with complex patterns (Multi-poles on OD, ID, end face (axial), radial, helical magnetization......)
4: Higher magnetic property (Br: 3500-8000G, BHmax: 3-12MGOe, Hcj: 4000-17000 Oe
5: Complicated shape
| COMPRESSION MOLDED BONDED NEODYMIUM GRADES | ||||||||
| Grade | Residual Induction | Coercive Force | Intrinsic Coercive Force | Maximum Energy Product | Density D | Reversible Permeability | Reversible Temp Coefficient A | Max Operating Temp |
| Br T(KG) | bHc KA/m (KOe) | iHc KA/m (KOe) | (BH)max KJ/m^3 (MGOe) | g/cm^3 | Br%/°C | |||
| BNP-2 | 300-400 | 160-240 | 440-600 | 19-26 | 5.6-6.0 | 1.2 | -0.11 | 160 |
| (3.0-4.0) | (2.0-3.0) | (5.5-7.5) | (2.4-3.3) | |||||
| BNP-3 | 400-510 | 216-280 | 504-680 | 24-32 | 5.6-6.0 | 1.2 | -0.11 | 160 |
| (4.0-5.1) | (2.7-3.5) | (6.3-8.5) | (5.6-6.0) | |||||
| BNP-4 | 460-520 | 224-288 | 504-680 | 30-35 | 5.6-6.0 | 1.2 | -0.11 | 160 |
| (4.6-5.2) | (2.8-3.6) | (6.3-8.5) | (3.8-4.4) | |||||
| BNP-5 | 470-550 | 240-360 | 520-680 | 37-44 | 5.6-6.0 | 1.2 | -0.11 | 160 |
| (4.7-5.5) | (3.0-4.5) | (6.5-8.5) | (4.7-5.5) | |||||
| BNP-6 | 550-650 | 320 - 376 (4.0 - 4.7) | 600-720 | 44-52 | 5.6-6.0 | 1.2 | -0.11 | 160 |
| (5.5-6.5) | (7.5-9.0) | (5.5-6.5) | ||||||
| BNP-7 | 550-650 | 320-408 | 560-680 | 52-64 | 5.6-6.0 | 1.2 | -0.11 | 160 |
| (5.5-6.5) | (4.0-5.1) | (7.0-8.5) | (6.5-8.0) | |||||
| BNP-8 | 620-670 | 400-456 | 640-800 | 64-76 | 5.8-6.2 | 1.2 | -0.11 | 160 |
| (6.2-6.7) | (5.0-5.7) | (8.0-10.0) | (8.0-9.5) | |||||
| BNP-8A | 620-680 | 400-480 | 1040-1280 | 65-73 | 5.8-6.1 | 1.2 | -0.1 | 180 |
| (6.2-6.8) | (5.0-6.0) | (13.0-16.0) | (8.2-9.2) | |||||
| BNP-9L | 670-730 | 360-416 | 520-640 | 68-75 | 5.8-6.1 | 1.2 | -0.11 | 120 |
| (6.7-7.3) | (4.5-5.2) | (6.5-8.0) | (8.6-9.4) | |||||
| BNP-9 | 650-700 | 416-456 | 680-800 | 68-76 | 5.8-6.2 | 1.2 | -0.12 | 160 |
| (6.5-7.0) | (5.2-5.7) | (8.5-10.0) | (8.5-9.5) | |||||
| BNP-9H | 650-700 | 432-488 | 920-1040 | 71-80 | 5.8-6.1 | 1.2 | -0.1 | 180 |
| (6.5-7.0) | (5.4-6.1) | (11.5-13.0) | (8.9-10.0) | |||||
| BNP-10H | 650-710 | 432-480 | 764-960 | 74-82 | 5.8-6.1 | 1.2 | -0.1 | 180 |
| (6.5-7.1) | (5.4-6.0) | (9.8-12.0) | (9.3-10.3) | |||||
| BNP-10 | 670-720 | 424-480 | 640-800 | 76-84 | 5.8-6.2 | 1.2 | -0.1 | 160 |
| (6.7-7.2) | (5.3-6.0) | (8-10) | (9.5-10.5) | |||||
| BNP-11 | 680-740 | 400-480 | 640-800 | 80-88 | 6.0-6.2 | 1.2 | -0.1 | 160 |
| (6.8-7.4) | (5.0-6.0) | (8-10) | (10-11) | |||||
| BNP-12D | 720-770 | 440-520 | 720-880 | 88-96 | 6.1-6.3 | 1.2 | -0.1 | 160 |
| (7.2-7.7) | (5.5-6.5) | (9.0-11.0) | (11.0-12.0) | |||||
| BNP-12L | 730-770 | 368-432 | 520-640 | 80-88 | 6.0-6.3 | 1.2 | -0.12 | 120 |
| (7.3-7.7) | (4.6-5.4) | (6.5-8.0) | (10.0-11.0) | |||||
| BNP-13L | 780-830 | 400-480 | 480-640 | 88-104 | 6.1-6.4 | 1.2 | -0.12 | 120 |
| (7.8-8.3) | (5.0-6.0) | (6.0-8.0) | (11.0-13.0) | |||||
| | ||||||||
| INJECTION MOLDED BONDED NEODYMIUM GRADES | ||||||||
| Grade | Residual Induction | Coercive Force | Intrinsic Coercive Force | Maximum Energy Product | Density D | Reversible Permeability | Reversible Temp Coefficient A | Max Operating Temp |
| Br T(KG) | bHc KA/m (KOe) | iHc KA/m (KOe) | (BH)max KJ/m^3 (MGOe) | g/cm^3 | Br%/°C | |||
| BNI-3 | 350-450 | 200-280 | ||||||