ss2205 stainless steel round bar ,s31803 polished round bar
Stainless steels are high-alloy steels. These steels are available in four groups that include martensitic, austenitic, ferritic and precipitation-hardened steels. These groups are formed based on the crystalline structure of stainless steels.
Stainless steels contain larger amounts of chromium in comparison with other steels and thus have good corrosion resistance. Most of the stainless steels contain about 10% of chromium.
Grade 2205 stainless steel is a duplex stainless steel whose design enables combining improved resistance to pitting, high strength, stress corrosion, crevice corrosion and cracking. Grade 2205 stainless steel resists sulfide stress corrosion and chloride environments.
The following datasheet provides an overview of grade 2205 stainless steel.
The chemical composition of grade 2205 stainless steel is outlined in the following table.
| Iron, Fe | 63.75-71.92 |
| Chromium, Cr | 21.0-23.0 |
| Nickel, Ni | 4.50-6.50 |
| Molybdenum, Mo | 2.50-3.50 |
| Manganese, Mn | 2.0 |
| Silicon, Si | 1.0 |
| Nitrogen, N | 0.080-0.20 |
| Carbon, C | 0.030 |
| Phosphorous, P | 0.030 |
| Sulfur, S | 0.020 |
Equivalent materials to grade 2205 stainless steel are:
ASTM A182 Grade F51
ASTM A240
ASTM A789
ASTM A790
DIN 1.4462
Grade 2205 stainless steel is annealed at 1020-1070°C (1868-1958°F) and then water quenched.
Grade 2205 stainless steel is hot worked in the temperature range of 954-1149°C (1750-2100°F). Hot working of this grade stainless steel under room temperature is recommended whenever possible.
Welding methods recommended for grade 2205 stainless steel include SMAW, MIG, TIG and manual covered electrode methods. During the welding process, the material should be cooled below 149°C (300°F) between passes and preheating of the weld piece should be avoided. Low heat inputs should be used for welding grade 2205 stainless steel.