High Toughness Weave Industrial Fire Hose , Heavy Duty Fire Hose 930 Psi

Nitrile Rubber Lay Flat Fire Hose Heavy Duty Through the Weave 6inch BP 930psi

Manufactured in accordance with NFPA 1961 standard, latest edition. within our ISO-9001 certified quality assurance system.

Construction: Circular polyester weave extruded internally and externally with NBR-PVC.

Hose shall be made from 100% high tenacity synthetic yarn circular woven and completely, protected and locked-in by tough highly resistant synthetic nitrile rubber, forming a single homogenous construction without the use of glues or adhesives of any type.

The ribs on the cover surface greatly increase abrasion resistance and help provide a long service life.

Lining Properties:
a. Ultimate Tensile Strength:
Tensile strength of the lining and cover shall not be less than 1500 psi (10,500 kpa ).
b. Ultimate Elongation:
400% minimum.
c. Accelerated Aging Test

The tensile strength and ultimate elongation of the vulcanized rubber compound which has been subjected to the action of oxygen at a pressure of 300 psi +/- 10 psi , (2100kpa +/- 70kpa) and temperature of 70 degrees centigrade +/-1 degree centigrade (158 F +/- 18 F ) for a period of 96 hours shall be , greater than 60% of the original properties stated.

Color:Yellow or Red
Temperature range:-5° to 200°F (-20° to 95°C)
Elongation at WP:<1.5%
Expansion at WP:<4%
Abrasion:6000 DIN cycles

Standard Length: 50ft, 100ft, 20m, 30m

Applications:

• Standby hoses in nuclear power station,

• Supply hoses in petrochemical refefineries.

Recommended for Fire Fighting Solution.

Comparable to

HFX of All American Hoses, etc.