High Performance RTV Silicone Sealant 9310 Ø For the sealing and bonding of LCD decorative lighting and LED lights.
● Product Features:
Ø Single component, room temperature curing, dealcoholization type.
Ø Neutral curing, becoming elastomer after curing.
Ø Alcohols released after curing, no irritant smell generated, non-corrosive to carbonate ester & copper materials.
Ø High thermal distortion and stress strain resistance.
Ø High temperature and humidity resistant.
Ø High performance on insulation, damp Proofing, vibration resistance, corona resistance, electricleakage resistance and chemical resistance.
● Main Applications:
Ø For the sealing and bonding of LCD decorative lighting and LED lights.
Ø For the bonding and sealing solar photovoltaic module.
Ø Suitable for outside environments.
● Specifications & Packages
Ø 310ml/cartridge, 25cartridges/carton.
● How to Use
Ø Keep the object surfaces clean without rusts, dusts and oil.
Ø Dispense the sealants to object surfaces.
Ø Put the objects in the air for 24 hours in the condition of room temperature & 55%RH to reach a cure depth of 2~4mm the longer, the deeper.
Ø The outlet of unspent adhesive should be sealed in time, clean the crusts on the outlet for another use within a short time, the performance of adhesive won’t be affected.
● Storage:
Ø Keep the sealant away from children.
Ø Use it in ventilated places
Ø In case of contact with skins, wipe and then flush with clear water.
Ø In case of contact with eyes, flush with clear water immediately and go to hospital for checking.
Ø Store it in dry and shady places at the temperature of 8~28℃
Storage life is 6 months from the date of manufacture
● Technical Data:
| Item | Unit | Typical Value | Range |
| Item No. | 9310 | ||
| Color | Semitransparent | ||
| Component of Basic Materials | Polysiloxane | ||
| Density | g/cm3 | 1.0 | 0.95~1.05 |
| Tack Free Time (25℃,50%RH) | min | 5 | 5~10 |
| Curing Type | Dealcoholization | ||
| Hardness | Shore A | 25 | 25±5 |
| Tensile Strength | Mpa | 0.4 | ≥0.4 |
| Elongation at break | % | 300 | ≥300 |
| Shear Strength | Mpa | 1.8 | 1.5~2.3 |
| Volume Resistivity | Ω*cm | 3.0×1015 | ≥1.0×1015 |
| Dielectric Strength | KV/mm | 22 | ≥20 |
| Work Temperature | ℃ | -40~150 |