Detailed Product Description
| Color: | B Translucent | Density: | B 0.92 |
| Viscosity: | 1000 | Mix Ratio By Weight (A:B): | 10:1 |
| Handing Curing Time: | 60 MINS | Tensile Strength: | 0.5MPA |
| Elongation At Break: | 170% | Hardness: | Shore A 12 |
| Work Temperature: | -60-200 |
4112 RTV Silicone Potting Sealant For the deep potting of power supply and electronic components and parts.
● Product Features:
Ø Double component, condensation type.
Ø Room temperature curing.
Ø Ethyl alcohol released after curing, non-corrosive to electronic components
Ø High adhesion to all electronic components except for those made of PP&PE.
Ø High performance on insulation, damp proofing, vibration resistance, chemical resistance, electricleakage resistance.
Ø No need to add primer coating before use
Ø High & low temperature resistant
Ø Flame retardant rating:UL94 V-1
● Main Applications:
Ø For the deep potting of power supply and electronic components and parts.
Ø Especially suitable for the potting of inside and outside LED displays that request for flame retardant.
| Item | Unit | Typical Value | ||
| Color | Component A | Translucent | ||
| Component B | Translucent | |||
| Component of Basic Materials | Polysiloxane | |||
| Density | Component A | g/cm3 | 0.95 | |
| Component B | 0.92 | |||
| Viscosity | Component A | mPa*s | 1200 | |
| Component B | 8 | |||
| After Mixed | 1000 | |||
| Mix Ratio by weight (A:B) | 10:1 | |||
| Handing Curing Time | min | 60 | ||
| Initial Curing Time | hour | 3 | ||
| Full Curing Time | hour | 72 | ||
| Tensile Strength | After Curing | Mpa | 0.5 | |
| Elongation at break | % | 170 | ||
| Hardness | Shore A | 12 | ||
| Volume Resistivity | Ω*cm | 1x1014 | ||
| Dielectric Strength | KV/mm | 25 | ||
| Flame Retardant Rating | UL94 V-1 | |||
| Work Temperature | ℃ | -60~200 | ||
● How to Use
Ø Before use, stir component A by hand or machine properly, keep component B sealed in the can and cut a proper hole at the sharp mouth of cartridge.
Ø Check whether it’s adhering to Applied Materials theoretically.
Ø Mix component A and B with the mix ratio A: B=10:1 by weight. Beforehand simple tests are requested if you need to change the mix ratio.
Ø Vacuum defoaming is not necessary if the potting thickness is below 5mm,but it is requested if the thickness is more than 5mm.
Ø Heating curing is unsuited, or pinholes and blisters will occur.
Ø Long-term exposure of component B in the air is unsuited.
● Packing:
Ø A: 5kg /bucket, B: 1kg/bucket.
● Storage:
Ø Keep it away from children.
Ø Use it in ventilated places
Ø In case of contact with skins, wipe and then flush with clear water.
Ø In case of contact with eyes, flush with clear water immediately and go to hospital for checking.
Ø Store it in dry and shady places at the temperature of 8~28℃
Ø Storage life: 12 months;