55-75℃ Low Temperature Hot Melt Adhesive Film for Bonding Leather
Hot Melt Adhesive Film Description
This product is a thermoplastic hot-melt adhesive film, which is
supported by release paper and can be repeatedly heated and
plasticized. This hot melt adhesive has excellent adhesion to
textiles, TPU, PVC, PC, ABS, and has low use temperature, easy
processing and excellent cold resistance.
Hot Melt Adhesive Film Technical Parameters:
Colour | Milky white translucent | Release Protection | Glassine Release Paper |
Proportion | 1.20±0.02g/cm³ | Thickness | 0.0125mm-0.15mm |
Opening time | 5min | Width | 5mm-1480mm |
Melt Flow Index | 37±10g/10mins (ASTM D1238-04) | Conventional Thickness | 0.05mm,0.08mm,0.10mm 0.12mm, 0.15mm |
Hardness | 97±3 (Shore A) | Conventional Width | 1380mm |
Melting Range | 55-75℃ (Tunsing DSC 214) | Conventional Length | 100 yards |
Activation Temperature | 77-116℃ (Tunsing) | Finished Product | 1380mm*100yards/roll |
Hot Melt Adhesive Film Technical Parameters:
First Lamination | Second Implanting | ||
Mechanical Mold Temperature | 90℃-110℃ | Mechanical Mold Temperature | 90℃-130℃ |
Time | 5-15 seconds | Time | 8-25 seconds |
Pressure | 0.3-0.6mpa | Pressure | 0.3-0.6mpa |
Hot Melt Adhesive Film Application
Customer feedback
Hot Melt Adhesive Film Package
It can ship by FedEX. It will need 5-7 days at usual. Also can by
sea and air.
3-5yards free sample for you to testing, you just pay to the
shipping fee.
Q1). Do you provide free sample? And how many days it will take?
Yes, of course.we provide free 3-5Y sample for your testing only need you to pay the shipping cost. We will make the sample within 3 working days and it will take 3-7days on the transportation., then you will have more confidence in our product quality and service,
Q2). How long is the lead time?
Sample lead time: 1-3 days Bulk lead time: 7-20days(depends on order quantity),
Q3). How do I pay for my order?
We usually accept L/C ,T/T ,Western Union , Paypal.