3.2mm Shrink To 1.5mm Black Heat Shrink Neoprene Tube Singel Wall
Heat Shrink Neoprene Tube
Dimensions
| Product No. | As S叩plied/mm | After Recovered/mm | |
| Inner diamter | Inner diamter | Wall thickness ** | |
| WRSLD-3.2/1.5 | N3.2 | W1.5 | 0.7±0.2 |
| WRSLD-4.8/2.5 | N4.8 | W2.5 | 0.8±0.2 |
| WRSLD-6.4/3.4 | N6.4 | W3.5 | 0.9±0.2 |
| WRSLD-9.5/5.4 | N9.5 | W5.4 | 1.0±0.2 |
| WRSLD-12.7/7.1 | 312.7 | <7.1 | 1.2±0.2 |
| WRSLD-15.8/8.7 | 315.8 | W8.7 | 1.3±0.3 |
| WRSLD-19.1/10.5 | >19.1 | W10.5 | 1.4±0.3 |
| WRSLD-22.2/12.5 | &22.2 | W12.5 | 1.7±0.3 |
| WRSLD-25.4/14.5 | >25.4 | W14.5 | 1.8±0.3 |
| WRSLD-31.8/18.0 | M31.8 | W18.Q | 2.2±0.3 |
| WRSLD-38.1/21.5 | >38.1 | W21.5 | 2.4±0.3 |
Features
• Made of cross linked chlorinated polyolefin
• Resistant to most fluids and solvents, including aviation and ground-vehicle fuels, lubricating oil, and hydraulicfluids
• Good flexibility at low temperature
• Resistant to abrasion and physical abuse while providing flexibility and strain relief
• Performance meets requirements of SAE-AMS-DTL-23053/1.
• Widely used for insulation, strain relief, and abrasion protection on cable harnesses and wire bundles in the military and aerospace industries.Especially suitable for applications requiring exposure to fluids and solvents at elevated temperatures.
• RoHS compliant
• Operation temperature: -45°C to 105°C
• Shrink temperature: start at 90°C, and fully recovered at 130°C
• Standard color: Black.
**Wall thickness will be less when shrinkage is restricted.
Technical Data
| I Property | Test Method | Typical Performance I |
| Tensile strength(MPa) | ASTM D412 | ^10.3 |
| Elongation at Break (%) | ASTM D412 | >225% |
| Tensile stress at 200% elongation (MPa) | ASTM D412 | <10.3 |
| Tensile Strength After Aging |
| (120°C,168hrs)(%) | SAE-AMS-DTL-23053 | N8.3 |
| Elongation at Break after Aging | ||
| (120°C,168hrs)(%) | SAE-AMS-DTL-23053 | >175% |
| Dielectric Strength (kV/mm) | ASTM D 2671 | >11.8 |
| Volume resistivity (Q-cm) | ASTM D 876 | >1x1011 |
| Flammability(Self extinguishing | ASTM D2671, | |
| 15 seconds; 3 inches) | Procedure A | |
| Fungus resistance | ASTMG21 | No growth |
| Low temperature flexibility | ・70°C,4 hrs | No cracking |