AISI 403 UNS S40300 Cold Rolled Stainless Steel Strip In Coil
403 stainless steel ( 13Cr- Low Silicon content type )
403 stainless is a corrosion and heat resistant 12% Cr martensitic stainless steel.
This material offers a wide range of mechanical properties that are obtainable by appropriate heat treatments.
It is easily hardened by oil, fan or air cooling and may be tempered at temperatures of up to 1350°F (732°C)
to improve fracture toughness. Oil or fan cooling is required in thicker sections.
403 stainless has a composition that falls within the limits designated for 410 stainless.
however, it has a tighter range of chromium content and lower maximum silicon and nickel contents.
This composition was developed to meet the exacting requirements of turbine blade constructions,
which demand a material that combines corrosion resistance with a high elastic limit and high impact strength.
The following table shows a comparison of the nominal composition of 403 stainless with that of 410 material.
Standard
| AISI | EN/DIN | JIS | GB |
403 S40300 | SUS403 | 1Cr12 | |
410 S41000 | 1.4006 X12Cr13 | SUS410 | 1Cr13 12Cr13 |
Chemical composition ( weight % )
| Grade | C | Si | Mn | P | S | Cr | Ni |
| 403 | 0.15 max. | 0.50 max. | 1.00 | 0.040 | 0.030 | 11.50~13.00 | 0.60 max. |
| 410 | 0.15 max. | 1.00 max. | 1.00 | 0.040 | 0.030 | 11.50~13.50 | 0.75 max. |
Heat treatment of 403 stainless steel
Annealing
403 stainless steel may be annealed at 1500-1650°F (816-899°C),
followed by a slow cool to 1100°F (593°C), and a final air cool.
Hardening
403 material may be fully hardened by oil quenching from
1650-1800°F (899-982°C).
Light sections may be hardened by air or fan cooling.
This alloy will harden, to varying degrees, when cooled from temperatures above
1500°F (816°C) unless it is slowly cooled to below the critical temperature or held for
sufficient length of time at a temperature below the critical temperature.
TEMPERING
Tempering may be done at a temperature between 400°F (204°C) and
1400°F (760°C),
but it is advisable to avoid the 800°F (427°C) to 1100°F (593°C) range due to a decrease in impact
properties and corrosion resistance.
Outside of this range, strength and hardness decrease while ductility and toughness increase as the
tempering temperature is raised.
Applications
403 stainless widely used for turbine blade, sealing strip.
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com