Deep Slope GM13 Standard Double Textured HDPE Geomembrane Sheet Anti Seepage Anti Slip
Quick Detail:
Production Description:
Textured Geomembrane is produced by the spray texture technology.
It is designed with one or two side textured surface. Except for
the excellent properties of smooth geomembrane.
HDPE textured geomembranes are available with either single- or double-sided textured surface which exhibit superior shear strength and the high multi-axial performance. The textured surface processing is the only one that produces a textured material without significant reduction of any physical properties. The product allows project for greater slopes to be designed since frictional characteristics are enhanced. Compared with smooth HDPE geomembranes, they have better friction features. The manufacturing of HDPE geomembrane textured contains approximately 97.5% polyethylene, 2.5% carbon black and trace amounts of anti-oxidants and heat stabilizers, no other additives, fillers or extenders are used. The textured surface is processed by spraying system.
Table 2(a) – High Density Polyethylene (HDPE) Geomembrane - Textured
| Properties | Test | Test Value | Testing | |||||||
| Method | Frequency | |||||||||
| 30 mils | 40 mils | 50 mils | 60 mils | 80 mils | 100 mils | 120 mils | (minimum) | |||
| Thickness mils (min. ave.) | D 5994 | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | per roll | |
| · | lowest individual for 8 out of 10 values | -10% | -10% | -10% | -10% | -10% | -10% | -10% | ||
| · | lowest individual for any of the 10 values | -15% | -15% | -15% | -15% | -15% | -15% | -15% | ||
| Asperity Height mils (min. ave.) (1) | D 7466 | 10 mil | 10 mil | 10 mil | 10 mil | 10 mil | 10 mil | 10 mil | every 2nd roll (2) | |
| Density (min. ave.) | D 1505/D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 200,000 lb | |
| Tensile Properties (min. ave.) (3) | D 6693 | 20,000 lb | ||||||||
| · | yield strength | Type IV | 63 lb/in. | 84 lb/in. | 105 lb/in. | 126 lb/in. | 168 lb/in. | 210 lb/in. | 252 lb/in. | |
| · | break strength | 45 lb/in. | 60 lb/in. | 75 lb/in. | 90 lb/in. | 120 lb/in. | 150 lb/in. | 180 lb/in. | ||
| · | yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | ||
| · | break elongation | 100% | 100% | 100% | 100% | 100% | 100% | 100% | ||
| Tear Resistance (min. ave.) | D 1004 | 21 lb | 28 lb | 35 lb | 42 lb | 56 lb | 70 lb | 84 lb | 45,000 lb | |
| Puncture Resistance (min. ave.) | D 4833 | 45 lb | 60 lb | 75 lb | 90 lb | 120 lb | 150 lb | 180 lb | 45,000 lb | |
| Stress Crack Resistance (4) | D 5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI GM10 | |
| (App.) | ||||||||||
| Carbon Black Content (range) | D 4218 (5) | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 20,000 lb | |
| Carbon Black Dispersion | D 5596 | note (6) | note (6) | note (6) | note (6) | note (6) | note (6) | note (6) | 45,000 lb | |
| Oxidative Induction Time (OIT) (min. ave.) (7) | 200,000 lb | |||||||||
| (a) Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | ||
| — or — | ||||||||||
| (b) High Pressure OIT | D 5885 | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | ||
| Oven Aging at 85°C (7), (8) | D 5721 | |||||||||
| (a) Standard OIT (min. ave.) - % retained after 90 days | D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 90 days | D 5885 | 80% | 80% | 80% | 80% | 80% | 80% | 80% | ||
| UV Resistance (9) | D 7238 | |||||||||
| (a) Standard OIT (min. ave.) | D 3895 | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (11) | D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | ||
Specification:
| Item | Properties | Unit | Thickness | |||||
| 1.0 | 1.25 | 1.5 | 2.0 | 2.5 | 3.0 | |||
| 1 | Roughness Height | mm | 0.25 | |||||
| 2 | Minimum Density | g/cm3 | 0.939 | |||||
| 3 | Breaking Strength | N/mm | 10 | 13 | 16 | 21 | 26 | 32 |
| 4 | Elongation at Break | % | 100 | |||||
| 5 | Right Angle Tear Strength | N | 125 | 156 | 187 | 249 | 311 | 374 |
| 6 | Puncture Strength | N | 267 | 333 | 400 | 534 | 667 | 800 |
| 7 | Stress Crack Resistance | Hrs | 300 | |||||
| 8 | Carbon Black Content (range) | % | 2.0-3.0 | |||||
| 9 | Low Temperature Impact Embrittlement at -70℃ | / | ok | |||||
| 10 | Water Vapor Permeability Coefficient(gNaN/cm2.s.p.a) | / | ≤1.0*10-13 | |||||
| 11 | Dimensional Stability | % | ±2 | |||||
Application:
Water Conservancy Projects: Anti-seepage, leaking stoppage and reinforce of river/lake/basin/dam, anti-seepage of water channel, vertical core wall, lake etc;
Aquaculture: Inner liner or fish pond, shrimp pond, revetment of sea cucumber pool etc;
Agriculture: Reservoir,drinking water pool, pool, irrigation system;
Advantage:
1. Long life, anti-aging, roof material can be more than 30 years,
underground can be more than 50 years.
2. Good tensile strength, high elongation.
3. Good high/low-temperature flexibility
4. Easy to construct, no pollution.
5. The good anti-corrosive ability can be used in the special area
6. Various colors are available
7. Skidproof