Wanshengli brand anti-seepage geosynthetic membrane hdpe geomembrane is made from 97.5% high density polyethylene (HDPE) and 2.5% Carbon black/anti-aging agent/anti-oxygen/UV absorbent/stabilizer and other accessory, which is widely used for fishpond,solid waste containment and water containment environment and mining environment. Anti-seepage HDPE geomembrana is made of best quality high density polyethylene (HDPE) with specially formulated and original polyethylene resin, combined with specified quantity carbon black, antioxidant, anti-aging agent and UV resistance components, which contributes to its excellent resistance to UV radiation and being suitable for different conditions.
Our Anti-seepage geosynthetic membrane hdpe geomembrane is produced by three layer co-extrusion technique by the most advanced automatical equipment. All the productions are manufactured according to US GRI standards and ASTM, complete specifications with superior quality. The width can reach 8m. Geosynthetic membrane is far more cost effective, environmental safety, excellent durability, chemically resistance, fast deployment and easy transportation than traditional concrete, asphalt and compacted clay.
Quick Detail:
Features:
1)High anti-seepage ratio:
HDPE geomembrane has a great anti-seepage effect unmatched by ordinary waterproof materials, and is recommended in some projects with high anti-seepage requirements.It's Permeability property is ≤1.0*10-13g●cm/(cm2●s●pa).
2)Chemical Stability:
It has excellent stability, acid and alkali resistance, salt solution, oil, alcohol, etc., and is mostly used in sewage treatment and landfills.
3)Anti plant root system
HDPE geomembrane has excellent puncture resistance and resists most plant roots. It is a must-choice product for planting roofs.
4)Aging resistance
HDPE geomembrane has excellent anti-aging, anti-ultraviolet, anti-decomposition capabilities. Oven aging at 85℃, standard OIT, 55% retained after 90 days, oven aging at 85℃,high pressure OIT, 80% retained after 90 days.
5)High Mechanic strength
It has good mechanical strength, and is first choice for seepage prevention in water conservancy projects. The tensile strength ,tear resistance, and puncture resistance properties all meet GRI-GM13 standard.
6)Low cost
Compared with other traditional materials, HDPE geomembrane has obvious cost advantages and is the best product for water storage and anti-seepage.
7)Environmental protection formulation
The raw materials used in Yingfan HDPE geomembrane have reached relevant international standards, and are non-toxic and environmentally friendly. Widely used in drinking water ponds, breeding ponds, etc.
8)Rapid construction
Compared with other traditional materials, HDPE geomembrane can be laid in a variety of forms to meet different construction requirements.
General Specification
| Thickness | 0.25mm | 0.35mm | 0.5mm | 0.75mm | 1.0mm | 1.25mm | 1.5mm | 2.0mm |
| Density g/m2 | ≥0.94 | |||||||
| Tensile yield strength (N/mm) | 3.75 | 5 | 7.5 | 11 | 15 | 18 | 22 | 29 |
| Tensile breaking strength (N/mm) | 6.75 | 13.5 | 19 | 20 | 27 | 33 | 40 | 53 |
| Elongation at yield(%) | ≥12 | |||||||
| Elongation at break(%) | ≥700 | |||||||
| Puncture strength(N) | 80 | 150 | 160 | 240 | 320 | 400 | 480 | 640 |
| Angle tear load | 31.25 | 45 | 62.5 | 93 | 125 | 160 | 190 | 250 |
| Carbon black content(%) | 2.0-3.0 | |||||||
| 85℃ aging after 90 days high pressure | 55 | |||||||
Parameters
| Properties | Test | Test Value | Testing Frequency | |||||||
| Method | 30 mils | 40 mils | 50 mils | 60 mils | 80 mils | 100 mils | 120 mils | (minimum) | ||
| Thickness (min. ave.) | D5199 | nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Per roll | |
| Lowest individual of 10 values | -10% | -10% | -10% | -10% | -10% | -10% | -10% | |||
| Density mg/l (min.) | D 1505/D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 200,000 lb | |
| Tensile Properties (1) (min. ave.) | D 6693 | 20,000 lb | ||||||||
| Yield strength | Type IV | 63 lb/in. | 84 lb/in. | 105 lb/in. | 126 lb/in. | 168 lb/in. | 210 lb/in. | 252 lb/in. | ||
| Break strength | 114 lb/in. | 152 lb/in. | 190 lb/in. | 228 lb/in. | 304 lb/in. | 380 lb/in. | 456 lb/in. | |||
| Yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | |||
| Break elongation | 700% | 700% | 700% | 700% | 700% | 700% | 700% | |||
| Tear Resistance (min. ave.) | D 1004 | 21 lb | 28 lb | 35 lb | 42 lb | 56 lb | 70 lb | 84 lb | 45,000 lb | |
| Puncture Resistance (min. ave.) | D 4833 | 54 lb | 72 lb | 90 lb | 108 lb | 144 lb | 180 lb | 216 lb | 45,000 lb | |
| Stress Crack Resistance (2) | D5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI-GM10 | |
| (App.) | ||||||||||
| Carbon Black Content (range) | D 4218 (3) | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 20,000 lb | |
| Carbon Black Dispersion | D 5596 | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | 45,000 lb | |
| Oxidative Induction Time (OIT) (min. ave.) (5) | 200,000 lb | |||||||||
| (a) | Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | |
| — or — | ||||||||||
| (b) High Pressure OIT | D 5885 | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | ||
| Oven Aging at 85°C (5), (6) | D 5721 | |||||||||
| (a) Standard OIT (min. ave.) - % retained after 90 days | D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 90 days | D 5885 | 80% | 80% | 80% | 80% | 80% | 80% | 80% | ||
| UV Resistance (7) | D 7238 | |||||||||
| (a) Standard OIT (min. ave.) | D 3895 | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (9) | D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | ||
Application:
Package:
Packaging Details:
Neutral package of Pond Liner Material
Roll Size: 5.8m*50m 100m
Or packed according to customers' requirements such as mark the company Logo
As example:
Specification 20ft container 40ft container
1.0mm size: 5.8m*100m 20GP 23rolls 20300sqm