JIS G4802 S65C-CSP Patented Spring Steel Strip

JIS S65C-CSP is CARBON STEEL, HIGH CARBON STEEL, STRUCTURAL STEEL.

Grade : S65C-CSP Classification: Structural steel

Standards: JIS G 4802 : Cold-rolled steel strip for springs

Dimensions and tolerances
Thickness: 0.1 to 5 mm; Tolerances: +/- 0.008 to 0.11 mm
Width: 10 to 400 mm; Tolerances: +/- 0.15 to 0.60
*accept nonstandard size, please contact with our sales.

Our Advantage
1. Precise thickness, uniform hardness. Bright surface, smooth edge.
2. High flatness of board surface, high performance after multiple bending.
3. No cracking after stamping, and the quality is stable. And we provide Self-Inspection Reports and Raw-Material Test Certificates.
4. Professional anti-rust protective packaging. On time delivery, competitive price.
5. Large stock available, no MOQ requiremen

S65C-CSP Patented Strip Chemical composition

S65C-CSP Patented Strip Mechanical properties

S65C-CSP Patented Strip Delivery condition

Cold rolled narrow steel strip covered by JIS G4802 shall be supplied in one of the following delivery conditions:

-annealed or annealed and skin passed(+A or +LC);

-cold rolled(+CR);

-quenched and tempered(+QT).

NOTE The delivery condition-annealed to achieve spheroidized carbides(+AC)-may be agreed. In such cases, limits on spheroidization and mechanical properties may also be agreed at the time of enquiry and order.

S65C-CSP Patented Strip Decarburization

For silicon alloyed steels, decarburization shall not exceed 3% of the material thickness per side,for non silicon alloyed steels, decarburization shall not exceed 2% of the material thickness per side when measure data distance of 5mm from the stripe edge

S65C-CSP Patented Strip Surface finish

The surface finish of cold rolled narrow steel strip shall be bright as produced by rolling and annealing in a controlled atmosphere.

The surface finishes of quenched and tempered cold rolled strip are as follows:

1 grey/blue oxide finish:unpolished;

2 brigth tempered:unpolished

3 polished: obtained by fine grinding, abrasive brushing or other processes;

4 polished and coloured:blue or yellow colour obtained by oxidization by heat

treatment.

S65C-CSP Patented Strip Mandatory information

The following information shall be supplied by the purchaser at the time of enquiry and order to enable the supplier to comply with the requirements of this European Standard:

a) the quantity to be delivered;

b) the designation of the product form (cold rolled narrow strip);

c) the number of the dimensional standard

d) the dimensions and tolerances on dimensions and shape and, if applicable, letters

denoting relevant special tolerances;

e)the number of this European Standard including the number of the relevant part;

f) steel name or steel number

g) the delivery condition

h) if required, the type of inspection document in accordance with EN 10204.

Equivalent Materials
DIN 1.0601DIN C60AFNOR CC55AFNOR C60BS 080A62BS 60CSBS 60HSBS En9BS 070M55BS C60BS 060A62UNI C60AISI 1060SAE 1060JIS S60CJIS S58CJIS SWRH62BEN C60EN 1.0601ISO C60ISO CS60GOST 2GOST 60GOST 60GGB/T 60GB/T CRB970GB/T U20602ASTM 1060UNS G10600DIN 1.1221DIN Ck60DIN C60EAFNOR XC60AFNOR C60RRAFNOR 9160C031AFNOR 9160/C25AFNOR XC65AFNOR C60EBS 070M60BS CS60BS C60ESS 16781064JIS S60CMJIS S65CMJIS S60C-CSPJIS S65C-CSPJIS 30AJIS 37AEN C60EEN C60SEN 1.1221ISO C60EISO C60E4ISO S58CGOST 60GAGB 60GB U20602UNS G10640

Material No.: S65C-CSP standard: JIS G4802 International steel grades: SAE:1070 JIS: S70CM Unalloyed steel for springs as belleville washers, spring plates and stabilizer bars for motor vehicles Hot forming and heat treatment: Forging or hot rolling: Normalising: Soft annealing: Hardening: 1100 - 800°C 810 - 840°C/air 680 - 710°C/furnace 815 - 845°C/oil min. 59 HRC or 670 HV as quenched

We hold expertise in providing a qualitative range of Patented Steel Strips to our clients at affordable prices. High carbon steel is an ideal material for custom flat springs, custom clips, and custom sheet metal stampings. High Carbon Steel Strips combines ease of fabrication with good strength and surface finish, is valued for its strength properties and operates at significantly higher levels than the mild steel grades. cold-rolled spring steel strips are gaining popularity in various industries. They are increasingly being implemented in engineering projects, through a fairly large number of small component manufacturers, parts and machine components.By making the right choice to buy steel strips, we reduce the amount of waste produced, thereby saving time and space. With a constant focus on the needs and requirements of our customers, we have created a unique offer.

S65C-CSP Patented Strip Inspection and testing

verification of the dimensions

visual examination of the surface quality

Chemical analysis

Extent of testing

Tensile and bending tests

Tolerances on shape