Off White Aqueous PFA Dispersion Liquid With MFR 5.1-10 SF-3201

PFA Dispersion SF-3201 with MFR 5.1-10

Product Description:

PFA dispersion is off-white aqueous perfluoroalkoxy stabilized with a non-ionic surfactant. It is a general-purpose dispersion that can be used to impart some of the unique properties of PFA to end products that would be difficult to make using traditional melt extrusion processes. It can be used to coat or impregnate porous structures or to make thin films. It can be coated and melt bonded to polytetrafluoroethylene (PTFE) resin or used as a hot melt adhesive.

The PFA resin in SF-3201 is a melt flowable thermoplastic, providing superior properties typical of

fluoroplastic resins: retention of properties after service at 260 °C and useful properties at –240 °C.

SF-3201 aqueous dispersion provides:

• Inertness to nearly all industrial chemicals and solvents

• Stability at high temperatures

• Excellent dielectric properties

• Excellent weatherability

• Excellent anti-stick properties

Applications:

• Heat-sealable top coatings for PTFE-coated fabrics for belting, circuit boards, architectural fabrics, and electrical insulation

• Cast film for capacitor dielectrics or chemical barriers

• Hot melt adhesive for PTFE, PFA, and FEP parts

• Metal coatings

Specification:

Processing:

Conventional coating techniques, such as dip, spray, spin, or roller coating, can be used for coating or impregnating high temperature materials with SF-301. Thin coats, usually less than 5 μm (0.2 mil), are applied to prevent mud cracking as the coating dries. The water is normally removed at 120 °C, followed by heating to remove the wetting agent (typically at 250–270 °C). Final consolidation is done above the 305 °C melt point.

If the SF-3201 is being used as a top coat over a PTFE coated fabric or other parts, the coating must be heated to melt the PTFE (approximately 337 °C) to maximize adhesion. Prolonged heating above 370 °C should be avoided, as this could lead to thermal degradation of the SF-3201 polymer.

Other solid or liquid ingredients can be added to SF-3201 to provide specific processing or finished product behavior.

Packaging, storage and handling:

SF-3201 is packaged in 25L(20kg) PE drums and 1,000-L(1250kg) IBC drum.

SF-3201 must be properly stored to maximize the stability of the dispersion. The PFA particles will

settle on prolonged standing and/or on prolonged heating; temperatures above 40 °C should be avoided. The dispersion must be protected from freezing, which will cause irreversible settling. The optimum storage temperature range is 7–24 °C. If dispersions are to be stored for extended periods, lower-temperature storage is desirable. For optimal performance, SF-301 should be gently mixed or rolled monthly and prior to use.

Ammonium hydroxide is used to set the pH to 9.5-11.0 at the time of shipment. High ambient temperatures can deplete the ammonium hydroxide level and reduce the PH. Declining PH eventually favors bacterial growth, which causes odor and scum. The PH of opened containers should be measured and maintained between 9.5 and 11.0.

High-speed stirring, pumping, or any other violent agitation should be minimized to prevent coagulation and to minimize foaming. Ideally, the dispersion should be conveyed by gravity from storage to processing stations.

Storage and handling areas should be clean. Keep dispersion drums closed and clean to avoid both contamination and coagulation by drying at the liquid surface. High processing temperatures will cause even very small foreign particles to become visible or to make defects in finished products. Good housekeeping and careful handling are essential.