Agricultural machinery or the parts for the black electrophoretic paint.
Product Introduction
HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
| Ideal for high demand for salt spray industry, such as pipe trench, auto chassis parts, castings. | The bath has strong anti-shrinkage and anti-pollution ability. | The appearance of the coating is flat, delicate, smooth. |
Main ingredients
| Pigment: carbon black, kaolin, antirust pigment | Solvent: alcohol ether |
| Additives: surface active agent, prevent shrinkage cavity agent | |
Bath on site management project
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
| Classification | Project | Control Data | Testing frequency | |
| New bath | Anolyte | |||
| Electrophoresis tank | Ratio | 1:6 | -- | |
| Ripening time | 24-48 | -- | ||
| Solid ( 120 ℃ /1h ,% ) | 14±4 | -- | once a day | |
| PH | 5.6-6.2 | 2.0-3.5 | once a day | |
| Conductivity ( μs/cm ) | 1200±400 | 2000±1000 | once a day | |
| P/B | 0.08-0.15 | once a week | ||
| L panel | Smooth horizontal plane and vertical plane without obvious differences | once a week | ||
| Solvent content (%) | 0.5-1.2 | once a week | ||
| Liquid level Fall head (cm ) | 10-15 | once a day | ||
| ED voltage( V ) | 0-300 | once a day | ||
| Break voltage ( V ) | ≥320 | once a week | ||
| Bath temperature ( ℃ ) | 30-36 | once a day | ||
| ED time( S ) | 60~180 | once a day | ||
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day | |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day | |
| Baking furnace | Provisions furnace temperature( ℃ ) | 185-195 | once a day | |
| Curing conditions | Drying temperature | (180-190)℃×(20-30)min (With content holding time) | once a day | |
Customers in the agricultural machinery industry