UT Multilayer Dental Zirconia Block 16 Color Zirconia Blank 49% Translucent

Active Member

Contact Us

[China]

Address: 101-201，Building 4，No.1 Branch of Zhongcheng Life Science Park, No. 14 Zhongxing Road, Xiuxin Community, Kengzi Street Office, Pingshan District, Shenzhen, China

Contact name:wenly

Shenzhen Yurucheng Dental Materials Co., Ltd

UT Multilayer Dental Zirconia Block 16 Color Zirconia Blank 49% Translucent

Country/Region	china
City & Province	shenzhen guangdong

Product Details

UT Multilayer Dental Zirconia Block 16 Color Zirconia Blank 49% Translucent

UT multilayer zirconia block and 16 color zirconium blocks for open zirconia blank and false zirconia blocks dental

Introduction of YUCERA's UT Multilayer high translucent dental zirconia:

UT multilayer zirconia blank is a dental multilayer zirconium oxide (4Y-TZP cervical, 5Y-TZP incisal) with natural color and translucency gradient and high flexural strength(700 MPa ), with as high as 49% translucent , monolithic restorations. The soft material before sintering ensures an effortless manufacturing process. All-ceramic veneering is possible with the common all-ceramic systems (see CET value).

It impresses with its perfect balance between translucency and strength for the production of aesthetic all-ceramic restorations. The soft material before sintering ensures an effortless manufacturing process.

Features of UT Multilayer high translucent zirconium oxide for perfect aesthetics dental zirconia/ceramics block/blank/discs:

1. Proven Aesthetics.
2. Comprehensive color selection – 20 colors ( 16 A-D, 3 Bleach).
3. Maximum variety of indications – from the single-tooth restoration to multi-unit bridge.

4. CAD CAM digital system

5. Bending Strength of zirconia disc 600 MPa

6. Translucency of zirconia disc 49%,

Indications
Single-tooth restorations (anterior and posterior)
3-unit bridges (anterior and posterior)
Multi-unit bridges (anterior and posterior)

Processing Options
1. Monolithic processing or partial ceramic veneering
2. Optional brush or dipping infiltration possible

Colors
A1, A2, A3, A3.5, A4
B1, B2, B3, B4
C1, C2, C3, C4
D2, D3, D4
OM1, OM2, OM3

Packaging
Single Disc

YUCERA all series

Type	Code	Translucency	Bending Strength	Hardness	Color	Size
White zirconia block	HT	40%	≧1200Mpa(Av.)	1200HV	White (coloring liquid with vita 16 shades and 26 shades	Open system& Zirkon zahn system & Amann Girrbach System
White zirconia block	ST	43%	≧1200Mpa(Av.)	1200HV	White (coloring liquid with vita 16 shades and 26 shades
Preshaded zirconia block	ST-Color	43%	≧1100Mpa(Av.)	1200HV	Vita 16 shades and BL1, BL2, BL3
Multilayer preshaded zirconia block	SHT-ML	46%	≧900Mpa(Av.)	1200HV
	UT-ML	49%	≧600Mpa(Av.)	1200HV
	3D Plus-ML	43%-57%	≧700Mpa(Av.)--1050Mpa(Av.)	1200HV

Suitable for below system

Open Cadcam System	Zironzahn System	Amann Girrbach
98x10mm	95x10mm	/
98x12mm	95x12mm	AGx12mm
98x14mm	95x14mm	AGx14mm
98x16mm	95x16mm	AGx16mm
98x18mm	95x18mm	AGx18mm
98x20mm	95x20mm	AGx20mm
98x22mm	95x22mm	AGx22mm
98x25mm	95x25mm	AGx25mm

SHT Multileyer/UT Multilayer /3D Multilayer Sintering Curve
Sintering step	Start Temperature(℃)	End Temperature(℃)	Time(Min)	Rate(℃/Min)
Step 1	20	900	90	9.7
Step 2	900	900	30	0
Step 3	900	1500	180	3.3
Step 4	1500	1500	120	0
Step 5	1500	800	60	-11.6
Step 6	800	natural cooling 20	120	-6.5