Item no.:B213
Material: aluminum alloy
Surface color: Nickel
Type: cabinet handle
Function: push and pull the drawer, cabinet door and decoration
etc.
Features: cute, colorful, high quality, durable, anti-rust
Available: various furniture, cabinet, dresser, closet, kitchen and
so on
Aluminum 4 properties
| Property | Metric value | Imperial value |
| Mechanical properties | ||
| Ultimate tensile strength | 317 MPa | 46,000 psi |
| Yield strength (0.2% offset) | 221—269 MPa | 32,000—39,000 psi |
| Impact strength | 61 J (7 J aged) | 45 ft-lbf (5 ft-lbf aged) |
| Elongation | 7% | |
| Shear strength | 214—262 MPa | 31,000—38,000 psi |
| Compressive yield strength | 414—600 MPa | 60,000—87,000 psi |
| Fatigue strength (rotary bending 5x108 cycles) | 48—57 MPa | 7,000—8,300 psi |
| Hardness | 91 Brinell | |
| Physical properties | ||
| Solidification range (melting range) | 380—386 °C | 716—727 °F |
| Density | 6.6 g/cm3 | 0.24 lb/in3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 108.9—113.0 W/m-K @ 100 °C | 755.6—784.0 BTU-in/hr-ft2-°F @ 212 °F |
| Electrical conductivity | 26-27% IACS | |
| Specific heat capacity | 418.7 J/kg-°C | 0.100 BTU/lb-°F |
| Property | Metric value | Imperial value |
| Mechanical properties | ||
| Ultimate tensile strength | 331 MPa (270 MPa aged) | 48,000 psi (39,000 psi aged) |
| Yield strength (0.2% offset) | 295 MPa | 43,000 psi |
| Impact strength | 52 J (56 J aged) | 38 ft-lbf (41 ft-lbf aged) |
| Elongation at Fmax | 2% | |
| Elongation at fracture | 3.6% (13% aged) | |
| Shear strength | 262 MPa | 38,000 psi |
| Compressive yield strength | 600 MPa | 87,000 psi |
| Fatigue strength (reverse bending 5x108 cycles) | 57 MPa | 8,300 psi |
| Hardness | 91 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Physical properties | ||
| Solidification range (melting range) | 380—386 °C | 716—727 °F |
| Density | 6.7 kg/dm3 | 0.24 lb/in3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 109 W/mK | 756 BTU-in/hr-ft2-°F |
| Electrical resistivity | 6.54 μΩ-cm at 20 °C | 2.57 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10−5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |