8MM SIZE IN 2000*6000MM PLATE SHEET HARDOX FOR Boiler Plate
Product Description
Hardox® 450 can be welded with all conventional arc welding methods
for ordinary and high-strength steel. Use welding consumables with
a yield strength of max.
500 MPa and a sufficiently low hydrogen content of max.
5ml/100 g of weld metal.The following consumables fulfill the
hydrogen criteria: • All solid wires applied at MAG (GMAW) and TIG
welding • MAG welding with flux cored wires (FCAW): Rutile and
basic types • MAG welding with metal cored wires (MCAW): Certain
types • SAW: Basic types of fluxes in combination with solid wires
Welding materials with these properties reduce residual stress
levels in the joint and its sensitivity to cold cracking.
Preheating can be avoided by welding with austenitic stainless
consumables according to type AWS 307 or AWS 309.
The wear-resistant steel plate is composed of a low-carbon steel
plate and an alloy wear-resistant layer. The alloy wear-resistant
layer is generally 1/3 to 1/2 of the total thickness. When working,
the matrix provides comprehensive properties such as strength,
toughness and plasticity against external forces, and the alloy
wear layer provides wear resistance that meets the requirements of
specified working conditions.
There is a metallurgical bond between the wear-resistant steel
plate alloy wear-resistant layer and the substrate. Through special
equipment and automatic welding process, the high hardness
self-shielding alloy welding wire is uniformly welded on the
substrate. The composite layer has one to two layers or even
multiple layers. During the composite process, due to the different
shrinkage ratio of the alloy, uniform transverse cracks appear. It
is a remarkable feature of wear-resistant steel plate.
The alloy wear-resistant layer is mainly made of chromium alloy,
and other alloy components such as manganese, molybdenum, niobium,
and nickel are also added. The carbides in the metallographic
structure are distributed in fibrous shape, and the fiber direction
is perpendicular to the surface. The microhardness of carbide can
reach above HV1700-2000, and the surface hardness can reach
HRC58-62. Alloy carbide has strong stability at high temperature,
maintains high hardness, and also has good oxidation resistance. It
can be used normally within 500°C.
Wear-resistant layer manifestations include narrow channels
(2.5-3.5mm), wide channels (8-12mm), curves (S, W), etc.; mainly
chromium alloys are used, and manganese, molybdenum, niobium,
nickel, and boron are also added And other alloy components, the
carbides in the metallographic structure are distributed in the
form of fibers, and the fiber direction is perpendicular to the
surface. The carbide content is 40-60%, the microhardness can reach
above HV1700, and the surface hardness can reach HRC58-62.
Wear-resistant steel plates are mainly divided into three
categories: general-purpose, impact-resistant and high-temperature
resistant types; the total thickness of wear-resistant steel plates
can reach 5.5 (2.5+3) mm as small as possible, and the thickness
can reach 30 (15+15) mm; Rolling small-diameter DN200
wear-resistant pipes can be processed into wear-resistant elbows,
wear-resistant tee, and wear-resistant reducer.
|
|
Grade | Tensile strength (Mpa) | Elongation (%)(min) | Hardness (HBW) | -20℃ Impact AKv/J (min) |
NM360 | ≥1100 | 12 | 330-390 | 24 |
NM400 | ≥1200 | 10 | 370-430 | 24 |
NM450 | ≥1250 | 7 | 420-480 | 24 |
NM500 | | | 470(min) | |
NM550 | | | 530(min) | |
NM600 | | | 570(min) | |
|
|
Grade | Yield strength (Mpa) | Hardness (HB) | Impact energy |
HARDOX400 | 900-1100 | 370-430 | 45J/-40℃ |
HARDOX450 | 1100-1300 | 425-475 | 50 J/-40℃ |
HARDOX500 | 1250-1400 | 470-540 | 37 J/-40℃ |
HARDOX550 | | 525-575 | 30 J/-40℃ |
HARDOX600 | | 550-640 | |
Our company can produce low alloy high strength abrasion resistant steels of
grade NM360, NM400, NM450, NM500, NM550 and NM600 which have high strength and good abrasion resistant properties,
good toughness and weldability, excellent processing properties and formability. Good performances of our company’s plates have
been positively proven in different climates, terrains and
environments.
These grades of plates are mainly applied for excavators, front
wheel loaders, tippers bodies, conveyers, chutes, containers,
crushers, fragmentizes, mixers, sieves, demolition tools and
barges. Our company’s abrasion resistant plates maximize the
abrasion
resistant performance of products, reduce the risk of accidental
shutdown and contribute to making precise equipment maintenance
plan as per different situations and the service of life is
doubled,tripled or even five times multiplied.in the mean time,the
plates can make the final products and machines get lighter weight
themselves,longer life and reduce emission of co2,because of the combination of material’s high hardness, good toughness and high
strength.
PACKAGE PER BUNDLE
1.Reinforcement of angle in steel wore rodcircles or according to
customer's requirements.
2.Package in PVC material or according to customer's requirements
SHIPPING
1.Delivery: Within 7-30 days after the confirmation of the order
2.Transport cargo to port by truck and will covered on the road and
also covered at port.
3.Shipping by bulk or container
Packaging | Standard seaworthy export packing, other types of packing can be
customized as every requirement. |
Shipping packaging | Bundled with firm steel straps, easy for loading and unloading. |
Shipping time | 5-7 work days after delivery |
Shipping way | BY SEA |
Shipping port | ShangHai |
Product show
Packing and delivery