ASTM A36 Carbon Steel Plate Hot Rolled Mild Steel Plate 8*2000*6000MM
Carbon structural steel plate refers to carbon steel with less than 0.8% carbon, which contains less sulfur, phosphorus and nonmetal inclusions than carbon structural steel, with better mechanical properties.
| Steel grade type | Carbon steel: |
|---|---|
| Standard | |
| Production specifications | Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings. |
| Mchining | Turning Milling Grinding Deep hole drilling: length max 9.8 meters. |
| Range of work | Round bar steel: 1mm to 2000mm Square-shape steel: 10mm to 1000mm steel Plate/sheet:0.08mm to 800mm Width: 10mm to 1500mm Lenth: We can supply any lenth based on the customer's requirement. Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm. |
| Heat treatment | Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing |
ASTM A36, >8 to 15 in. thick, as-rolled steel plate
Categories: Metal; Ferrous Metal; ASTM Steel; Carbon Steel; Low
Carbon steel
Material Notes: A popular "workhorse" grade, it is used widely for
various applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.85 g/cc | 0.284 lb/in³ | Typical of ASTM steel |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 119 - 159 | 119 - 159 | based on conversion from tensile strength |
| Hardness, Rockwell B | 67.0 - 83.0 | 67.0 - 83.0 | based on conversion from tensile strength |
| Tensile Strength at Break | 400 - 552 MPa | 58000 - 80000 psi | |
| Tensile Strength, Yield | >= 221 MPa | >= 32000 psi | |
| Elongation at Break | >= 18.0 % | >= 18.0 % | in 8" |
| >= 21.0 % | >= 21.0 % | in 2", > 24" W | |
| Bend Radius, Minimum | 0.500 t | 0.500 t | ≤3/4" W; ASTM A6 PARA. S14 |
| 1.00 t | 1.00 t | >3/4 to 1" W; ASTM A6 PARA. S14 | |
| 1.50 t | 1.50 t | >1 to 1-1/2" W; ASTM A6 PARA. S14 | |
| 2.50 t | 2.50 t | >1-1/2 to 2" W; ASTM A6 PARA. S14 | |
| 3.00 t | 3.00 t | >2" W; ASTM A6 PARA. S14 | |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | <= 0.290 % | <= 0.290 % | |
| Copper, Cu | >= 0.020 % | >= 0.020 % | |
| Iron, Fe | >= 98.0 % | >= 98.0 % | |
| Manganese, Mn | 0.85 - 1.20 % | 0.85 - 1.20 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | 0.15 - 0.40 % | 0.15 - 0.40 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
| Properties | Conditions | ||
|---|---|---|---|
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 7.7-8.03 | 25 | |
| Poisson's Ratio | 0.27-0.30 | 25 | |
| Elastic Modulus (GPa) | 190-210 | 25 | |
| Tensile Strength (Mpa) | 1158 | 25 | oil quenched, fine grained, tempered at 425°C |
| Yield Strength (Mpa) | 1034 | ||
| Elongation (%) | 15 | ||
| Reduction in Area (%) | 53 | ||
| Hardness (HB) | 335 | 25 | oil quenched, fine grained, tempered at 425°C |
| Properties | Conditions | ||
|---|---|---|---|
| T (°C) | Treatment | ||
| Thermal Conductivity (W/m-K) | 42.7 | 100 | |
| Specific Heat (J/kg-K) | 477 | 50-100 | |
| Quantity | Value | Unit |
|---|---|---|
| Thermal expansion | 16 - 17 | e-6/K |
| Thermal conductivity | 16 - 16 | W/m.K |
| Specific heat | 500 - 500 | J/kg.K |
| Melting temperature | 1370 - 1400 | °C |
| Service temperature | 0 - 500 | °C |
| Density | 8000 - 8000 | kg/m3 |
| Resistivity | 0.7 - 0.7 | Ohm.mm2/m |