Reinforced Composite Hard Felt - Sheet
Features:
Composite Hard Felt is an ideal thermal insulation material for vacuum quenching furnace, vacuum brazing furnace, vacuum sintering furnace, and vacuum series high-temperature furnace,good thermal insulation performance, rapid deformation and rapid cooling without deformation.
Our Reinforced Composite Hard Felt are flat plates, drums, dishes and other shaped parts, which are widely used in furnaces with high vacuum and inert gas, such as: single crystal growth furnace, polycrystalline ingot furnace, sapphire crystal growth furnace, cemented carbide (powder Metallurgy) vacuum sintering furnace, low-pressure sintering furnace, etc., the maximum operating temperature can reach 3000 ℃. In addition to its excellent thermal insulation efficiency,
Reinforced Composite Hard Felt also has the characteristics of installation without support,
easy installation / removal, etc., which not only saves labor, but also reduces the replacement cycle.
The density of Reinforced Composite Hard Felt is 0.18-0.32g/cm3.
The Composite Hard Felt surface can be coated with graphite paper or carbon cloth, carbon cloth and graphite paper, graphite paper can be sandwiched between each felt. It can prevent surface fluff, gas leakage (convection), and protect its surface (prevent loss) and increase the strength of hard felt.
Composite Hard Felt has the advantages of high rigidity, self-supporting, high strength, no short fiber loss, and low thermal conductivity that traditional insulation materials do not have.
Physical and chemical indicators:
| main material | PAN-CF / asphalt-CF / viscose-CF | Sheet specifications | length(mm) | 10-3000 |
| Bulk density(g/CM3)) | 0.25-0.30 | width(mm) | 10-2000 | |
| Thermal conductivity | 0.15-0.25(25℃)0.40-0.45(1400℃)
| thickness(mm) | 5-300 | |
Barrel specifications | diameter(Φ) | Φ100-Φ2500 | ||
| Carbon content(％) | ≧98 | Wall thickness(T) | 5-150 | |
| bending strength(Gpa) | 1.8-3.5 | Tube height | 100-3000 | |
| Flexural strength(Gpa) | 1.5-2.8 |
Use environment | air(℃) | ≦350 |
| ash content(ppm) | ≦300 | vacuum(℃) | ≦2200 | |
| Processing temperature | First ≧1800 Second ≧2200 | Inert atmosphere(℃) | ≦3000 |
Temperature resistance: 2200 ℃ in vacuum, 3000 ℃ in inert gas