Product Description of Fire Resistant High Alumina Refractory Brick
Alumina Firebricks For Kiln & Boiler With High Refractoriness
& Strength
High alumina brick is a kind of neutral refractory with alumina
content above 48%. It is formed by shaping and calcining bauxite or
other raw materials with high alumina content. High thermal
stability and fire resistance above 1770 ℃.
Product Features of Fire Resistant High Alumina Refractory Brick Alumina Firebricks For
Kiln & Boiler
1.High alumina bricks has properties of high refractoriness, high
strength, acid and washing erosion resistance, good thermal
stability and so on.
2.. Low bulk density, low thermal conductivity, good thermal
insulation performance.
3.High compressive strength.
4. Refractory category allow direct contact of fire, suitable ofr
various atmosphere
5. Long service life, easy operation.
Product Applications of High Alumina Bricks
High alumina bricks are widely used in cement, glass building
materials, steel smelting, petrochemical and other industries.
1.Iron & steel making industry: Blast furnace,hot blast
stove,electric furnace,ladle,tundish,heating furnace,refining
furnace,reheating furnace,annealing furnace,cupola furnace.
2.Non-ferrous Metal industry:Smelting furnace,refining
furnace,reverberatory furnace,converter furnace.
3.Building materials industry:Cement kiln,glass kiln,ceramic
kiln,lime kilns,kiln car,tunnel kiln.
4.Energy & Incineration:Coke oven,circulating fluidized bed
boiler,carbon roasting furnace, incinerators.
5.Others:Petrochemical industry furnace.
In addition, high alumina bricks can also be processed into open
hearth regenerative grid bricks, socket bricks for pouring system,
nozzle bricks, etc. according to the requirements of industrial
furnaces.
Product Specification of High Alumina Refractory Bricks
Item | Index |
SK40 | SK38 | SK37 | SK36 | SK35 |
LZ-80 | LZ-75 | LZ-65 | LZ-55 | LZ-48 |
Al2O3 % | ≥80 | ≥75 | ≥65 | ≥55 | ≥48 |
Apparent Porosity, % | ≤21 | ≤24 | ≤24 | ≤22 | ≤22 |
CCS, MPa | ≥70 | ≥60 | ≥50 | ≥45 | ≥40 |
0.2MPa RUL ℃ | ≥1530 | ≥1520 | ≥1500 | ≥1450 | ≥1420 |
PLC, % | 1500℃×2h -0.4~0.2 | 1450℃×2h -0.4~0.1 |