Mill finish Aluminum Alloy 6063 Sunflower Shape Heat Sink Aluminum Extrusion Profile
| Alloy | 6063 |
| Temper | T3 - T8 |
| Thickness |
General profiles thickness:0.8 - 5.0 mm;
|
| Color Thickness | Anodized protection thickness: 8 - 10μm Powder coating protection thickness: 40-80μm |
| Length | 5.8-6.0m, or as cuostomer request |
| Color | Natural Color |
| Finish | Mill finish , anodize, powder coating , elecrophoresis , PVDF coating, all kinds of high simulation wood grain processing , etc. |
| Sample delivery | 2 Weeks |
| Deep Processing | Cutting , punching . |
| Delivery | 3-4 Weeks |
| Markets We Sold | Australia , Germany , North America , Africa and European countries and Southeast Asian area |
Advantages of the extrusion process
| ||
The extrusion process provides virtually unlimited opportunities for aluminium product shapes. Costs are cut by designing fewer components, which reduce fabrication and simplify assembly.
| ||
| These features and benefits are unmatched by other materials and processes | ||
| Complex integral shapes | High Quality | Low costs |
| Design flexibility | Versatility in joining | Machinable |
| Free Sample | Short lead times | Wide range of finishes |
Mechanical Properties of Sections under Room Temperature
Alloy |
State | Tensile strength test | Hardness test | ||||||||
| Tensile strength Rm M pa | Non-proportional Stretching Stress | Stretching rate | Pattern thickness | HV | HW | ||||||
| Rp0.2Mpa | (A50mm%) | mm | HV | HW | |||||||
| 6063 | T4 | 130 | 75 | 14 | - | ||||||
| T5 | 160 | 110 | 8 | 0.8 | 58 | 8 | |||||
| T6 | 205 | 180 | 8 | - | |||||||
6061 | T4 | 184 | 110 | 16 | - | ||||||
| T6 | 265 | 245 | 8 | - | |||||||
6082 (6351) | T4 | 205 | 110 | 12 | - | ||||||
| T6 | 290 | 250 | 6 | - | |||||||
Questions & Answer
Q1: What is aluminum extrusion, fabrication, and anodization?
A: Aluminum Extrusion refers to a process of creating shapes with
an aluminum billet or log by forcing it to flow through a shaped
opening in a die. Aluminum can be extruded into standard shapes or
specific designs depending on a customer’s preference.
Aluminum Fabrication refers to building aluminum components by cutting, drilling, slotting, tapping,bending, CNC machining, mechanical assembly and welding.
Aluminum Anodization is an electro-chemical process of coating
aluminum with a thin layer of oxide to increase corrosion
resistance and harden the surface.
Aluminum also can be dyed with various anodizing colours,which in
most widely used is Brone shades.
Q2: What’s the thickness for anodizing? Can you do 15um?
A: Our normal thickness is about 10 um. Yes, we can do 15um and
above.
Q3: What color you can do for powder coating? The thickness for
powder coat?
A: We can do any color for powder coat as long as you can provide
the color sample. Our normally powder coating thickness is 60-80um.
Q4: What’s the delivery time for samples and mass production?
A: (1). 2 weeks to open the new moulds and make samples.
(2). 3-4 weeks after receipt of deposit and
confirmation of the order.
About us :
Foshan Kaiya Aluminum Co., Ltd is a comprehensive and professional enterprise integrating research, design production and sales of aluminium extrusion profiles for construction and industrial applications. There are currently 24 aluminum extrusion process lines at 500MT TO 2500MT, 5 process lines for anodizing, 3 process lines for powder coating, 2 process line for painting, 2process line of polishing and brushing. We still have 2 packing line. Our annual production capacity has reached 80,000 tons which is at the forefront of the aluminium industry in China.