5052 H32 H34 Aluminium Flat Strips Sheet High Elongation For Armor Cable

Active Member

Contact Us

[China]

Address: D41-1/01 BLOCK,D FENQU,XIPENG ZUTUAN,XIANGTANG VILLAGE,XIPENG TOWN,JIULONGPO DISTRICT,CHONGQING

Contact name:Masha Cui

Chongqing Dongchong Aluminum Co., Ltd.

5052 H32 H34 Aluminium Flat Strips Sheet High Elongation For Armor Cable

Country/Region	china
City & Province	chongqing chongqing
Categories	Aluminum Strips

Product Details

5052 H32 H34 High Quality Aluminum Flat Strip for Cable and Armor Cable

Product specification

Type	Aluminium strip
Material	5000 Series:5005,5025,5040,5052,5056,5083,5A05,5050 etc.
Temper	H12, H14, H16, H18, H22, H24, H26 ,H111,H112,T4,T6,T5,O
Specifications	Thickness 0.006-200mm or as your required Width :6mm-1200mm or as your required.Length:1000-6000mm or as your required
Surface	Bright, polished, hair line, brush, sand blast, checkered, embossed, etching
Standard	ATSTM B209, JIS H4000-2006,GB/T3190-2008,GB/T3880-2006
Trade Information	Packaging Details:Wooden pallet,Wooden box
	Delivery Detail:3-5days for stock, 10-15days for normal size,25-30days for customized size
	MOQ :500kg-5000kg according to different products
	Supply Ability:10000tons per month
	Payment terms: TT,LC

The 5000 series of aluminium alloys represent 5052, 5005, 5083 and 5A05 series. The 5000 series aluminium bar belongs to the more commonly used alloy aluminium plate series, the main element is magnesium, the content of magnesium is between 3-5%. It can also be called Al-Mg alloy. Its main characteristics are low density, high tensile strength, high elongation and good fatigue strength, but it can not be strengthened by heat treatment. In the same area, the weight of Al-Mg alloy is lower than that of other series. It is also widely used in conventional industry. In our country, 5000 series aluminium sheet belongs to one of the more mature aluminium sheet series.

Chemical Compostion

Alloy 5052
Temper	Specified Thickness, mm		Tensile Strength, MPa		P		Elongation, min, %c
Temper	over	through	min	P	min	P	in 50 mm	in 5x Diameter (5.65 $)
O	0.15	00.32	170	215	5		13
	0.32	00.63	170	215	65		15
	0.63	01.20	170	215	65		17
	1.20	06.30	170	215	65		19
	6.30	80.00	170	215	65		18	16
H32d	0.40	00.63	215	265	160		4
or	0.63	01.20	215	265	160		5
H22D	1.20	03.20	215	265	160		7
	3.20	06.30	215	265	160		7
	6.30	50.00	215	265	160		11	10
H34d	0.20	00.32	235	285	180		3
or	0.32	00.63	235	285	180		3
H24D	0.63	01.20	235	285	180		4
	1.20	03.20	235	285	180		6
	3.20	06.30	235	285	180		6
	6.30	25.00	235	285	180		10	9
H36d	0.15	00.32	255	305	200		2
or	0.32	00.63	255	305	200		3
H26d	0.63	01.20	255	305	200		4
	1.20	04.00	255	305	200		4
H38d	0.15	00.32	270		220		2
or	0.32	00.63	270		220		3
H28D	0.63	01.20	270		220		4
	1.20	03.20	270		220		4
H112	6.30	12.50	190		110		7
	12.50	40.00	170		65			10
	40.00	80.00	170		65			14
H322	0.50	01.20	215	240	145		5
	1.20	02.90	215	240	145		7
	2.90	03.20	215	240	145		9
	6.30	80.00

Chemical Composition

Alloy	Temper	Thickness(mm)	Tensile strength(Mpa)	Yeild strength(Mpa)	Elongation(%)
Alloy	Temper	Thickness(mm)	Min
5052	H111 O	>0. 20 — 0. 50	170 — 215	65	12
		>0. 50 — 1. 50			14
		>1.55 — 3.00			16
		>3. 00 — 6. 00			18
		>6.00 — 12. 50	165-215		19
		>12. 50 — 50.00	165-215		—
	H12	>0. 20 — 0. 50	210 — 260	160	4
		>0.5-1.5			5
		>1.50 —3.00			6
		>3, 00 — 6. 00			8
	H14	>0. 20 — 0. 50	230-280	180	3
		>0.50-1.50			3
		>1. 50 -3. 00			4
		>3.00 — 6.00			4
	H16	>0. 20 — 0, 50	250—300	210	2
		>0. 50 — 1. 50			3
		>1. 5- 3.0			3
		>3.00 — 4. 00			3
	H18	>0. 20-0.50	270	240	1
		>0. 50 — 1. 50			2
		> 1.50 — 3.00			2
	H22 H32	>0. 20—0. 50	210 — 260	130	5
		>0. 50-1.50			6
		>1.50 — 3.00			7
		>3. 00 — 6. 00			10
	H24 H34	>0. 20 — 0. 50	230 — 280	150	4
		>0.50 — 1. 50			5
		>1,50 — 3.00			6
		>3.00 — 6.00			7
	H26 H36	>0. 20 — 0.50	250 — 300	180	3
		>0. 50 — 1, 50			4
		>1.50—3.00			5
		>3. 00—4. 00			6
	H38 H28	>0. 20 — 0, 50	270	210	3
		>0. 50~1. 5			3
		>1. 50 — 3. 00			4
	H112	>6.00—12. 50	190	80	7
		>12. 50 — 40,00	170	70
		>40, 00 — 80, 00	170	70