2.78 G/Cc Density Seamless Aluminum Round Pipe High Corrosion Resistance 2024 T3

Contact Us

[China]

Trade Verify

Address: No. 2-4-1, Building#18, Lvcheng Street No.97, Xipeng Town, Jiulongpo District, Chongqing401326, P.R. China

Contact name:Oliver ZHOU

Chongqing Huanyu Aluminum Material Co., Ltd.

Verified Suppliers

Trust
Seal
Verified
Supplier
Credit
Check
Capability
Assessment

2.78 G/Cc Density Seamless Aluminum Round Pipe High Corrosion Resistance 2024 T3

Country/Region	china
City & Province	chongqing

Product Details

High Corrosion Resistance 2024 T3 Seamless Aluminum Round Tubing

2024 seamless aluminum tubing

2024T3 round tubing has high strength and excellent fatigue resistance which is used to advantage on structures and parts where a good strength-to-weight ratio is desired

Physical Properties

	Metric	English	Comments

Density	2.78 g/cc	0.1 lb/in³	AA; Typical
Mechanical Properties

Hardness, Brinell	47	47	AA; Typical; 500 g load; 10 mm ball
Ultimate Tensile Strength	186 MPa	27000 psi	AA; Typical
Tensile Yield Strength	75.8 MPa	11000 psi	AA; Typical
Elongation at Break	20 %	20 %	AA; Typical; 1/16 in. (1.6 mm) Thickness
Elongation at Break	22 %	22 %	AA; Typical; 1/2 in. (12.7 mm) Diameter
Modulus of Elasticity	73.1 GPa	10600 ksi	AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus.
Ultimate Bearing Strength	345 MPa	50000 psi	Edge distance/pin diameter = 2.0
Bearing Yield Strength	131 MPa	19000 psi	Edge distance/pin diameter = 2.0
Poisson's Ratio	0.33	0.33
Fatigue Strength	89.6 MPa	13000 psi	AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen
Machinability	30 %	30 %	0-100 Scale of Aluminum Alloys
Shear Modulus	28 GPa	4060 ksi
Shear Strength	124 MPa	18000 psi	AA; Typical
Electrical Properties

Electrical Resistivity	3.49e-006 ohm-cm	3.49e-006 ohm-cm	AA; Typical at 68 Degrees F
Thermal Properties

CTE, linear 68 Degrees F	23.2 µm/m- Degrees C	12.9 µin/in- Degrees F	AA; Typical; Average over 68-212 Degrees F range.
CTE, linear 250 Degrees C	24.7 µm/m- Degrees C	13.7 µin/in- Degrees F	Average over the range 20-300 Degrees C
Heat Capacity	0.875 J/g- Degrees C	0.209 BTU/lb- Degrees F
Thermal Conductivity	193 W/m-K	1340 BTU-in/hr-ft²- Degrees F	AA; Typical at 77 Degrees F
Melting Point	502 - 638 Degrees C	935 - 1180 Degrees F	AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater. Eutectic melting is not eliminated by homogenization.
Solidus	502 Degrees C	935 Degrees F	AA; Typical
Liquidus	638 Degrees C	1180 Degrees F	AA; Typical
Processing Properties

Annealing Temperature	413 Degrees C	775 Degrees F
Solution Temperature	256 Degrees C	493 Degrees F

Hot Products

Tapered 5083 H112 Aluminum Round Tubing Highly Resistant To Seawater Chemical Corrosion

Tapered 5083 H112 Aluminum Round Tubing Highly Resistant to Seawater Or Chemical Corrosion ...

2.78 G/Cc Density Seamless Aluminum Round Pipe High Corrosion Resistance 2024 T3

High Corrosion Resistance 2024 T3 Seamless Aluminum Round Tubing 2024 seamless aluminum tubing ...

High Corrosion Resistance Aluminum Round Tubing Easily Welded 6063 T4 Aluminum Tube Pipe

Excellent Corrosion Resistance And Can Be Easily Welded , 6063 T4 Extruded Aluminum Tube Aluminum ...

1060 Alloy Aluminum Hollow Aluminum Rods Low Strength High Purity

Aluminum Round Tubing Made out of 1060 Aluminum Alloy 1000 series alloy displays excellent forming, ...

5052 H34 Aluminum Round Tubing / Structural Aluminum Tubing 3.8mm Wall Thickness

Aluminum Round Tubing Made out of 5052H34 Aluminum Alloy 5052 aluminum alloy is highly resistant to ...

Protective Structures 6061 Aluminum Round Tubing / Aluminium Round Pipe

High Weight-To-Strenght 6061 Aluminum Round Tubing Widely Utiliazed In Protective Structures 6061 ...

Related Products