1.5*75mm Fecral Alloy 0cr21al6 Heating Resistance Strip
0Cr21Al6
Chemical Content(%)
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max0.06 | Max 0.025 | Max 0.025 | Max0.70 | Max 1.0 | 19.0~22.0 | Max 0.60 | 5.0~7.0 | Bal. | - |
Mechanical Properties
| Max Continuous Service Temp | 1250ºC |
| Resisivity at 20ºC | 1.42±0.07 ohm mm2/m |
| Density | 7.16 g/cm3 |
| Thermal Conductivity | 63.2 KJ/m·h·ºC |
| Coefficient of Thermal Expansion | 14.7×10-6/ºC |
| Melting Point | 1500ºC |
| Tensile Strength | 637~784 Mpa |
| Elongation | Min 12% |
| Section Variation Shrink Rate | 65~75% |
| Repeatedly Bend Frequency | Min 5 times |
| Continuous Service Time | - |
| Hardness | 200-260HB |
| Micrographic Structure | Ferrite |
| Magnetic Property | Magnetic |
Description: I
T is made of the surface resistance to high temperature insulation
treatment of iron chrome aluminum heating element.
Feature:
When used in the 1000 centigrade, there is almost no volatile
matter. Being used between 1000 centigrade and 1250 centigrade, the
voltatile is less and transparent. It has a long service life used
in high temperature. Thermal efficiency increased by more than 20%.
Usage:
It is widely used in all kinds of electric heater and heating
equipment.
Especially suitable for making such as high temperature far
infrared radiator, electric oven devices such as the heating
element.
The main performance
1. Can be arbitrary direction installed and used.
2. There is no need of protective atmosphere or vacuum protection,
assembly is convenient, low cost, use security.
3. Heating up fast, high thermal efficiency, temperature
uniformity.
4. Service life: 10000--500000 hours.
Grade | Highest temperature | Resistivity | Melting point | Tensile strength | Elongation |
0Cr21Al4 | 1100ºC | 1.23±0.06μΩ.m | 1500ºC | 750 | ≥12 |
0Cr25Al5 | 1250ºC | 1.42±0.07μΩ.m | 1500ºC | 750 | ≥12 |
0Cr23Al5 | 1300ºC | 1.35±0.06μΩ.m | 1500ºC | 750 | ≥12 |
0Cr21Al6NbCo | 1350ºC | 1.43±0.07μΩ.m | 1510ºC | 750 | ≥12 |
0Cr27Al7Mo2 | 1400ºC | 1.53±0.07μΩ.m | 1520ºC | 750 | ≥10 |