0Cr27Al7Mo2 Iron-chromium-aluminium alloy resistance heating wire for electric stove and spring heating
General Description
FeCrAl alloy is made by a high-temperature, ferritic
iron-chromium-aluminium alloy which can be used at temperatures up
to 1350degrees. Typical applications for 0Cr21Al6Nb are as
electrical heating elements in high-temperature furnaces in the
heat treating, ceramics, glass, steel, and electronics industries.
Feature:
With long service life.Heating up fast.High thermal
efficiency.Temperature uniformity. Can use vertically. When being
used in the rated voltage,there is no volatile matter.It is an
environmental protection electric heating wire. And an alternative
to the costly nichrome wire.Can be customized according to customer
requirements
FeCrAl alloys are characterized by excellent oxidation resistance and very good form stability resulting in long element life.
They are typically used in electrical heating elements in industrial furnaces and home appliances.
Fe-Cr-Al alloy with high resistivity and serviceability temperature than that for NiCr alloy and also has lower price.
Applications
0Cr21Al6 Iron-chrome-aluminium electric resistor strip is widely used for making electric heating elements in home appliances and industrial furnaces. Typical applications are flat irons, ironing machines, water heaters, plastic moulding dies, soldering irons, metal sheathed tubular elements and cartridge elements
application area
Our products are widely used in heat treatment equipment, auto parts, iron and steel manufacturing,
aluminum industry, metallurgical equipment, petrochemical equipment, glass machinery, ceramic machinery,
food machinery, pharmaceutical machinery, and power engineering industry.
Chemical Content, %
| Alloy material | Chemical composition % | |||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | others | |
| max(≤) | ||||||||||
| 1Cr13Al4 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 12.5-15.0 | — | 3.5-4.5 | Rest | — |
| 0Cr15Al5 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 14.5-15.5 | — | 4.5-5.3 | Rest | — |
| 0Cr25Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 23.0-26.0 | ≤0.60 | 4.5-6.5 | Rest | — |
| 0Cr23Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 20.5-23.5 | ≤0.60 | 4.2-5.3 | Rest | — |
| 0Cr21Al6 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 19.0-22.0 | ≤0.60 | 5.0-7.0 | Rest | — |
| 0Cr19Al3 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 18.0-21.0 | ≤0.60 | 3.0-4.2 | Rest | — |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.60 | 21.0-23.0 | ≤0.60 | 5.0-7.0 | Rest | Nb add0.5 |
| 0Cr27Al7Mo2 | 0.05 | 0.025 | 0.025 | 0.2 | ≤0.40 | 26.5-27.8 | ≤0.60 | 6.0-7.0 | Rest | |
Main technical characteristics of FeCrAl Alloy:
Brand Property | 1Cr13Al4 | 1Cr21Al4 | 0Cr21Al6 | 0Cr23Al5 | 0Cr25Al5 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Major chemical component% | Cr | 12.0-12.5 | 17.0-21.0 | 19.0-22.0 | 20.5-23.5 | 23.0-26.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 2.0-4.0 | 5.0-7.0 | 4.2-5.3 | 4.5-6.5 | 5.0-7.0 | 6.0-7.0 | |
| Fe | Balance | Balance | Balance | Balance | Balance | Balance | Balance | |
| Re | Appropriate | Appropriate | Appropriate | Appropriate | Appropriate | Appropriate | Appropriate | |
| Addition Nb:0.5 | Addition Mo:1.8-2.2 | |||||||
| Component max. use temperature | 950 | 1100 | 1250 | 1250 | 1250 | 1350 | 1400 | |
| Melting Point | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1510 | |
| Density g/cm3 | 7.40 | 7.35 | 7.16 | 7.25 | 7.10 | 7.10 | 7.10 | |
| Resistivity μΩ·m,20 | 1.25±0.08 | 1.23±0.06 | 1.42±0.07 | 1.35±0.06 | 1.45±0.07 | 1.45±0.07 | 1.53±0.07 | |
| Tensile Strength Mpa | 588-735 | 637-784 | 637-784 | 637-784 | 637-784 | 637-784 | 684-784 | |
| Extension rate% | 16 | 12 | 12 | 12 | 12 | 10 | ||
| Repeated bending frequency | 5 | 5 | 5 | 5 | 5 | |||
| Fast lift h/ | - | 80/1300 | 80/1300 | 50/1350 | ||||
| Specific Heat J/g. | 0.490 | 0.490 | 0.520 | 0.460 | 0.494 | 0.494 | 0.494 | |
| Heat Conduction Coefficient KJ/M.h | 52.7 | 46.9 | 63.2 | 60.1 | 46.1 | 46.1 | 45.2 | |
Linear expansion coefficient aX10-6/ (20-1000) | 15.4 | 13.5 | 14.7 | 15.0 | 16.0 | 16.0 | 16.0 | |
| Hardness HB | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Microstructure | Ferritic | Ferritic | Ferritic | Ferritic | Ferritic | Ferritic | Ferritic | |
| Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |