Customized Industrial Wear Resistance Alumina Ceramic Tube
Description:
Alumina(Aluminum Oxide, Al2O3) is the most extensively used advanced ceramic material due to their outstanding property characteristics and cost-effective advantage. As with the purity increases, both wear resistance and corrosion resistance also increases, so alumina are grouped together based on purity levels, including 95% alumina, 99% alumina, 99.5% alumina, 99.8% alumina, 99.9% alumina.
Alumina ceramic tubes generally used as a kind of standard
protection part.Our vast, readily-available inventory allows us to
supply our customer's ceramic tube needs immediately, even for
hard-to-find or specialty products.
Technical Parameters:
| Test item/Unit | Numerical Value | Test item/Unit | Numerical | ||||
| Product Material | Alumina | Zirconia | Product Material | Alumina | Zirconia | ||
| Component Content % | ≥99% | ≥95% | ≥90% | Volume Resistance MM | >1012 | >1012 | >1012 |
| Sintering Temp ℃ | 1780-1800 | 1650-1680 | 1550-2600 | Bending Strength Mpa | 400 | 320 | 1100 |
| Specific Gravity g/cm3 | ≥3.8 | ≥3.6 | >6 | Thermal Expansion Coefficient'10' | 6.8-8.0 | 6.2-8.5 | 6.9-10 |
| Breakdown Voltage Strength kv/mm | 15 | 15 | 15 | Roughness um | ≤0.8 | ≤0.8 | ≤0.8 |
| Bibulous Rate% | <0.01 | <0.01 | <0.01 | Mirror Polished Ra | ≤0.05 | ≤0.1 | ≤0.05 |
| Anti Pressure Mpa | 3700Mpa | 2400Mpa | 5000Mpa | Thermal Conductivity W/m.k | 25 | 20 | 25 |
| Hardness Hra | ≥88 | ≥82 | ≥88 | Temperature Resistance ℃ | 1700 | 1600 | 1800 |
Advantages:
1. High refractoriness;
2. Good thermal shock resistance;
3. Good creep-resisting property;
4. Good chemical stability;
5. Good high temperature strength and volume stability.
6. High erosion resistance
Application:
1. mining industry.
2. Cement industry.
3. Coal handling industry.
4. Steel industry.
5. Port industry.
More pictures: