Red Alumina Ceramic Accessories Duckbill Shape Nozzle

Product Overview

Alumina ceramics have better conductivity, higher mechanical strength and high temperature resistance. As a welding nozzle made of alumina ceramics, it has excellent high temperature resistance, high melting point, and no decline in mechanical properties. It can be used at high temperatures without affecting product performance or bursting. Good corrosion resistance, regardless of strong acid (except hydrofluoric acid), strong alkali (except hot alkali), inorganic organic salts and other conditions will not be affected.

Product parameter table

Alumina ceramic is a ceramic material with alumina as the main body, which is used for thick film integrated circuits.

Size	Part Number	Length (mm)	Orifice (in)	Orifice (mm)	Torchdesign
NO 4	10N50	47	1/4	6.5	17/18/26
NO 5	10N49	47	5/16	8.0	17/18/26
NO 6	10N48	47	3/8	9.5	17/18/26
NO 7	10N47	47	7/16	11.0	17/18/26
NO 8	10N46	47	1/2	12.5	17/18/26
NO 10	10N45	47	5/8	16.0	17/18/26
NO 12	10N44	47	11/16	19.5	17/18/26

Material Project				Alumina AL203	Silicon carbide sic	Silicon nitride sin	Silicon nitride sin
Color				Ivory	black	black	Milky white, gray black
Content(%)				99.5	……	……	……
Main features				Excellent high frequency electrical insulation Good wear resistance preservative Strong High hardness	Good high temperature strength High thermal conductivity Strong alkali resistance Wear-resistant Lightweight	Good high temperature strength Strong impact resistance Strong corrosion resistance Lightweight	High strength and high impact resistance Good self-lubricating Strong alkali resistance Smooth surface Good toughness
The main purpose				Wear parts High temperature parts Corrosion resistant parts	Machinery Seal Sliding parts High temperature parts	Molten metal parts Metal plasticity Processed parts	Industrial knives Pump parts Wear parts
Density			Kg/m³	3.9*10	3.16*10	3.3*10	6.0*10
Mechanical behavior	Vickers hardness		Gpa	16.0	23.0	14.0	13.2	12.7
	Flexural strength		Mpa	360	450	1020	1000	1470
	Compressive strength		Mpa	2350	……	……	……	……
	Fracture toughness		Mpa	4	2-3	7	4-5	4-5
Thermal performance	Linear expansion coefficient	40-400℃	×10^-5/℃	7.2	3.7	2.8	10.5	10.8
	Linear expansion coefficient	40-800℃	×10^-5/℃	8.0	4.4	3.3	11.0	11.3
	Thermal conductivity		W/(m·k)	32	200	27	3	3
	Specific heat		J/(kg·k)	0.78*10	0.67*10	0.65*10	0.46*10	0.46*10
	Thermal shock resistance (in water)		℃	250	……	＞800	300	350
Electrical performance	Dielectric strength		V/m	15*10⁵	……	13*10⁵	11*10⁵	……
	Volume resistance(20℃)		Ω·cm	＞10¹⁴	10⁸	10¹⁴	10¹³	……
	Dielectric constant		……	9.6	……	9.9	33	……
	Loss factor		×10^-4	10	……	……	520	……

Product advantages

Argon arc welding alumina welding ceramic nozzle series has the characteristics of high temperature resistance, strong reliability and price concessions.
Alumina ceramic nozzle can be used at 1500℃, with high strength, good thermal stability, corrosion resistance at high temperature, and excellent nozzle material performance.