Cobalt 32 Rod ERCoCr-F Welding Rod - Cobalt Based Alloy Welding Hard Facing Rod Pump Sleeves Fluid Valve
Product Description
WLCo F rod is a titanium calcium type coating, surfacing electrode with cobalt chromium tungsten alloy cores, should adopt DCRP. Surfacing metal can keep good abrasion resistance and corrosion resistance at 650 degrees.
It is used in the work of 650 degrees Celsius should be able to maintain good wear resistance and a certain degree of corrosion resistance of the occasion; for example, the high temperature and high pressure welding valve and hot shear knife, the impact of hot and cold staggered place.
Hardness: 40-45HRC
Chemical Composition(%)
C | Si | Mn | Mo | Cr | W | Ni | Fe | Co |
1.7 | ≤2.0 | ≤0.5 | ≤1.0 | 26.00 | 12.5 | 22.0 | ≤3.0 | Rest |
Packing Details
For length 350mm 500mm pack in carton each 5kg
For 1000mm packing in 5kg tube, 4 tubes in one 20kg carton
For length more than 1000mm, pack in wooden box directly
Applications
high temperature and high pressure welding valve and hot shear knife, the impact of hot and cold staggered place.
Type We Could Offer
| Trademark | Nominal Chemical Composition | HRC | Application | |||||||||
| C | Cr | Si | W | Ni | Fe | Mn | Mo | Co | B | |||
| WL Co1 | 2.45 | 30.0 | 1.0 | 13.0 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 50-58 | Valve seat insets, bearing, sawteeth, rotary ring, Pump Sleeves | |
| WL Co3 | 2.4 | 30.5 | 1.0 | 13.0 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 50-56 | Valve seat insets,steel mill guide roll, wearing panel of cracker blade, etc. | |
| WL Co4 | 1.0 | 31.0 | 1.0 | 14.0 | ≤3.0 | ≤1.0 | ≤0.5 | ≤0.5 | Bal. | 45-50 | Hot extrusion die, dry battery industry | |
| WL Co6 | 1.2 | 29.0 | 1.0 | 4.5 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 40-46 | Engine valve, high temperature valve, turbine blade | |
| WL Co12 | 1.4 | 30.0 | 1.3 | 8.5 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 44-50 | Pressure valves, sawteeth screw fights | |
| WL Co20 | 2.5 | 32.0 | 1.0 | 17.0 | ≤3.0 | ≤3.0 | ≤0.5 | ≤1.0 | Bal. | 54-59 | Wear plate, bearing sleeve, etc. | |
| WL Co21 | 0.2 | 27.0 | 1.0 | 0.2 | ≤3.0 | ≤2 | ≤1.0 | ≤5.5 | Bal. | 20-40 | Fluid valve seat, turbine blades, hot forging die | |
| WL Co25 | 0.05 | 20.0 | 1.0 | 15.0 | 10.0 | ≤2.0 | ≤1.5 | ≤1.0 | Bal. | 24 | High temperature and corrosion-resistant valve sealing surface, pressure casting dies, etc. | |
| WL Co31 | 0.5 | 26.0 | 1.0 | 7.5 | 10.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 30-35 | Extrusion die, steam turbine blade, etc. | |
| WL Co32 | 1.8 | 26.0 | 1.2 | 12.0 | 22.0 | ≤1.5 | ≤0.5 | ≤1.0 | Bal. | 40-45 | Engine inlet and exhaust valve | |
| WL Co190 | 3.2 | 26.0 | 1.0 | 14.0 | ≤1.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 54-60 | Petroleum drill bit, mining industry | |
| WL CoT400 | 0.08 | 8.5 | 2.6 | 1.5 | ≤1.5 | ≤1.0 | 28 | Bal. | 0.8 | 50-60 | Valve and roller path, plastic extruder in strongly corrosive | |
| WL CoT800 | 0.08 | 18.0 | 3.4 | ≤1.5 | 1.5 | ≤1.0 | 28 | Bal. | 0.8 | 52-58 | Valve and roller path, plastic extruder in strongly corrosive | |