WAL1 WAL2 WAL Pure Tungsten Wire Surface Black / Polished / Ground For Lamp Bulbs
Tungsten is the most widely used of the refractory metals. In wire form, it is essential for the production of lighting products such as wire filament, and other goods where its high temperature properties are of use. Among its properties are a melting point of 3410° C, a low coefficient of thermal expansion and low vapor pressure at elevated temperatures, along with good electrical and thermal conductivity.
Specification of WAL Tungsten Wires:
1, Diameter: 0.01mm~2.00mm
2, Grade: WAL1, WAL2,
3, Density: Purity 99.92%
4, Quality standard: GB/T 4181-1997(tungsten wire)ASTM B760-86
5, Specific electrical: 0.055 Ohm x mm2/m resistance at 20 °C.
6, Modulus of elasticity: 410 kN/mm2, at 20 °C.
Method of Use on WAL Tungsten Wires:
1. Aquadag layer on the surface of wire should be removed before using the wire is not suitable for contacting with iron, nickel, carbon, when the temperature is higher than 1000 . The wires should be preserved in dry room, in which the relative humidity should not surpass 65%, and keeping away from acid or alkali atmosphere.
2. Cleaned wires should be preserved in dry vessels
Tolerance of WAL Tungsten Wires:
Finished form | Specified diameter | Minimum length, mm | Diameter tolerance |
|---|---|---|---|
Wrought | 2.8≤d<5.0 | 600 | ± 2% |
5.0≤d<6.5 | 300 | ||
6.5≤d<11.0 | 200 | ||
Straightened | 0.8≤d<1.0 | 1000 | ± 2% |
1.0≤d<3.0 | 800 | ||
Ground | 0.8≤d<3.0 | 800 – 1000 | ±0.03mm |
3.0≤d<6.5 | 300 – 600 | ±0.05mm | |
6.5≤d<10.0 | 200 | ±0.08mm |
Tungsten Material Types and Applications:
Type | Name | Kind | Applications |
WAL1 | Nonsag tungsten wires | L | Used in making single coiled filaments, filaments in fluorescent lamps and other components. |
B | Used in making coiled coil and filaments in High power incandescent bulb, stage decoration lamp, heating filaments, halogen lamp, special lamps etc. | ||
T | Used in making special lamps, exposition lamp of copy machine and lamps used in automobiles. | ||
WAL2 | Nonsag tungsten wires | J | Used in making filaments in incandescent bulb, fluorescent lamp, heating filaments, spring filaments, grid electrode, gas-discharge lamp, electrode and other electrode tubes parts. |
Type | Kind | Tungsten content (%) | Total amount of impurity (%) | The content of each element (%) | Kalium content (ppm) |
WAL1 | L | >=99.95 | <=0.05 | <=0.01 | 50~80 |
B | 60~90 | ||||
T | 70~90 | ||||
WAL2 | J | 40~50 | |||
Note: Kalium should not be taken as impurity, and tungsten powder must be have been washed by acid. | |||||
Picture Show: