60.01mm(2.36260"), High Quality Chrome Steel Balls For Big Bearing,
G40 Or G60
Introduction
High-carbon chromium bearing steel refers to high-carbon alloy steel with a chromium content of 1.40-1.65%. The structure is relatively uniform and stable after heat treatment , with good wear resistance, high stress fatigue strength, good dimensional stability and good hardenability, and extremely strict control of sulfur and phosphorus. It is high-grade high-quality steel. Cold working mold steel. Specific gravity: 7.81.
This steel can meet the processing requirements under general working conditions. The brand numbers of ordinary high-carbon chromium bearing steel are GCr15 and GCr15SiMn. The performance of these two types of bearings is basically the same. But the hardenability of GCr15SiMn is better than GCr15, so GCr15SiMn is used for relatively large bearing parts.
Because GCr15SiMn has high crack sensitivity and low impact resistance, it cannot fully meet the requirements of thick-walled bearings and mining bearings. Therefore, the railway department does not allow the use of CGr15SiMn on passenger car bearings. It is also limited to thick-walled rolling mills and mining machinery under large and compact loads.
Chrome steel is a bearing grade alloy steel. This material is known as 52100 steel in the US, 100Cr6 in Europe, SUJ2 in Japan and GCr15 in China. This fine-grain martensitic steel has high hardness, exceptional wear, surface characteristics and is exceptional for the creation of chrome steel balls. Chrome steel is an excellent material for balls used in various applications such as food grinding systems, vibratory finishing, linear motion components, and check valves.
The surface of our chrome steel balls is extremely precise and smooth, ensuring that you will not find any defects such as flatness, dents, soft spots and cuts.
We mainly produce chrome steel with sizes ranging from 7.9375mm to
82.55mm. The main material is high chromium GCR15 or GCR15SiMn. Our
balls are mainly used in the wind energy industry.Our products enjoy high evaluation and satisfaction among
customers.
Our services and advantages
| Special types of balls supplied. |
| Small MOQ with competitive price. |
| Fast delivery based on quality guaranteed. |
| Small quantity of free samples could be provided. |
| Normal have in stock within one week can be shipped. |
Parameter
| Ball Diameter | Grade | Hardness | Material |
| 60.01mm(2.36260") | G40 or G60 | HRc 60-67 | GCr15SiMn,100CrSiMn6-4,SUJ3,52100 |
Product Details
| Product Name | High Quality Chrome Steel Balls |
| Size range | Ø 59.94 mm – Ø 60.06 mm(GCr15SiMn/SUJ3/100CrMn6 Chrome Steel Balls) |
| Quality grades | G40 or G60 for balls Ø59.94mm to 60.06mm |
| Hardness | For 60mm group ball, a minumun core hardness at centre of the ball shall be HRc55. minumun hardness at surface of the ball shall be HRc60. minumun hardness at depth of 15% ball diameter shall be HRc58. |
| Application | The High Quality Chrome Steel Balls are mainly applied in slewing ring bearing for wind turbines,such as single/double row ball bearing,single cross roller bearing,three roller bearing, double row angular contact ball bearing.Turntable bearing,Thrust ball bearing,Wheel hub bearing. |
Grade and Tolerance
| Precision / Grade | Ball Diameter Tolerance | Deviation from Spherical Form | Maximun surface roughness | Lot diameter variation |
| G40 | 1 | 1 | 0.06 | 2 |
| G60 | 1.5 | 1.5 | 0.08 | 3 |
| Chemical Composition | ||||||
| C% | Si% | Mn% | Cr% | Cu% | C% | |
| 52100 | 0.98~1.10 | 0.15~0.35 | 0.25~0.45 | 1.30~1.60 | 0.98~1.10 | |
| GCr15 | 0.95~1.05 | 0.15~0.35 | 0.25~0.45 | 1.40~1.65 | 0.25 | 0.95~1.05 |
| GCr15SiMn | 0.95~1.05 | 0.45~0.75 | 0.95~1.25 | 1.40~1.65 | 0.25 | 0.95~1.05 |
| 100Cr6 | 0.93~1.05 | 0.15~0.35 | 0.25~0.45 | 1.35~1.60 | 0.93~1.05 | |
| SUJ2 | 0.95 or 1.10 | 0.15 or 0.35 | 0.50 max | 1.30~1.60 | 0.95 or 1.10 | |