Hastelloy C2000 Alloy Steel Sheet C2000 Material Hastelloy C2000 Composition
Hastelloy C-2000 UNS N06200, Mostversatile, corrosion resistant alloy with excellent resistance touniform corrosion in oxidizing or reducing environments. Excellentresistance to stress corrosion cracking and superior resistance tolocalized corrosion as compared to C-276 alloy.
The nickel-chromium-molybdenum(Ni-Cr-Mo) C-type alloys have a long history of use in the ChemicalProcess Industries and are known for their versatility. Not only do theyresist all acids (especially hydrochloric, sulfuric, and hydrofluoric)over large temperature ranges, but they also resist the insidious typesof attack induced by chlorides and other halide solutions, specificallypitting, crevice attack, and stress corrosion cracking.
Wrought Hastelloy C-2000 is made of a NiCrMo alloy including copper. Highly versatile alloy C2000 prevents stress corrosion cracking and corrosion by different types of chemicals such as sulphuric acid, hydrochloric acid and hydrofluoric acids. Unlike other Hastelloy alloys, Nickel 2000 is resistant to both oxidizing and reducing conditions.
Nickel-Chromium-Molybdenum C type alloys have been traditionally used in the chemical processing sectors. These metals not only resist the corrosion by strong acids at whole temperature limits, even also prevent the detrimental attack by chlorides and other halide media.
Industrial Nomenclatures: Hastelloy C-2000, Alloy C2000, UNS N06200, NiCr23Mo16Cu, Werkstoffblatt 539, DIN 2.4699
| Wire | Sheet | Strip | Pipe | Rod | Fittings |
| SB 574/B 574, Kennblatt 9679.00 | SB 575/B 575 | SB 575/B 575 | SB 619/B 619, SB 622/B 622, SB 626/B 626, SB 462/B 462 | SB 574/B 574 | SB 366/B 366 |
Hastelloy C2000 can be easily welded by shielded metal arc welding, gas tungsten arc welding and gas metal arc welding methods. The unsuitable welding techniques are Oxy-acetylene and submerged-arc welding.
Post weld stress reduction up to 1202oF or 650oC is unsuitable for Hastelloy alloys. However this kind of heat processing is not important, but if followed, a complete solution annealing at 1149oC or 2100oF then water cooling should be done.
Forms Produced
| Hastelloy C-2000 Alloy Wire | Hastelloy C-2000 Alloy Wire Mesh |
| Hastelloy C-2000 Alloy Strip | Hastelloy C-2000 Alloy Sheet/Plate |
| Hastelloy C-2000 Alloy Rod/Bar | Hastelloy C-2000 Alloy Pipe/Tube |
| Hastelloy C-2000 Alloy Flanges | Hastelloy C-2000 Alloy Foil |
we can offers all above forms of Hastelloy C-2000 in all standard as well as custom specifications.